Chin-San Wu

To enhance the various properties of polyvinyl alcohol (PVA), varying concentrations of carboxy-functionalized graphene (CFG) were employed in the preparation of CFG/PVA nanocomposite films. FTIR and XRD analyses revealed that CFG, in contrast to graphene, not only possesses carboxylic acid group but also exhibits higher crystallinity. Mechanical testing indicated a notable superiority of CFG addition over graphene, with optimal mechanical properties such as tensile and yield strengths being achieved at a 3% CFG concentration. Relative to pure PVA, the tensile strength and yield strength of the composite increased by 2.07 and 2.01 times, respectively. XRD analysis showed distinct changes in the crystalline structure of PVA with the addition of CFG, highlighting the influence of CFG on the composite structure. FTIR and XPS analyses confirmed the formation of ester bonds between CFG and PVA, enhancing the overall performance of the material. TGA results also demonstrated that the presence of CFG enhanced the thermal stability of CFG/PVA nanocomposite films. However, analyses using scanning electron microscopy and transmission electron microscopy revealed that a 3% concentration of CFG was uniformly dispersed, whereas a 6% concentration of CFG caused aggregation of the nanofiller, leading to a decrease in performance. The incorporation of CFG significantly enhanced the water vapor and oxygen barrier properties of PVA, with the best performance observed at a 3% CFG concentration. Beyond this concentration, barrier properties were diminished owing to CFG aggregation. The study further demonstrated an increase in electrical conductivity and hydrophobicity of the nanocomposites with the addition of CFG. Antibacterial tests against E. coli showed that CFG/PVA nanocomposites exhibited excellent antibacterial properties, especially at higher CFG concentrations. These findings indicate that CFG/PVA nanocomposites, with an optimized CFG concentration, have significant potential for applications requiring enhanced mechanical strength, barrier properties, and antibacterial capabilities.

This research delves into the impact of incorporating thermally treated oyster shell powder (TOS), a biowaste filler, into low-density polyethylene (LDPE) to develop a LDPE/TOS blend, aiming at enhancing food packaging materials. The LDPE/TOS blend portrays advantageous characteristics such as augmented mechanical strength, thermostability, crystallinity, water absorption, and improved hydrophobicity with TOS content up to 50%. Microstructure analysis reveals a transition from a sparse to a more interconnected structure, contributing to the amplified tensile strength. The blend demonstrates increased barrier properties against water vapor transmission, which is attributed to elongated diffusion paths induced by the TOS particles. Application of the blend material in vegetable preservation trials manifested a substantial reduction in water loss compared to pure LDPE or no packaging. This biowaste-based blend film extends the shelf-life of chicken significantly when compared to that of pure LDPE. Importantly, the LDPE/TOS blend exhibits excellent antibacterial properties against both Escherichia coli and Staphylococcus aureus.

Nano zinc oxide-decorated graphene (G-ZnO) was blended with polyphenylene sulfide (PPS) to improve its tensile, thermal, crystalline, and barrier properties. The properties of neat PPS and PPS/G-ZnO nanocomposites were characterized and compared using various tests, including tensile tests, scanning electron microscopy, X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, evaluation of Escherichia coli inhibition, and barrier performance. The results demonstrated that G-ZnO played a crucial role in heterogeneous nucleation and reinforcement. When the concentration of G-ZnO was 0.3%, the tensile strength, elongation at break, thermostability, crystallinity, and water vapor permeability coefficients (WVPC) approached their maximum values, and the microscopic morphology changed from the original brittle fracture to a relatively tough fracture. In addition, when G-ZnO was added to PPS at a ratio of 0.3%, the tensile strength, elongation at break, and WVPC of PPS were increased by 129%, 150%, and 283%, respectively, compared to pure PPS. G-ZnO endowed the nanocomposites with antibacterial properties. The improvement in barrier performance can be attributed to three reasons: (1) the presence of G-ZnO extended the penetration path of molecules; (2) the coordination and hydrogen bonds between PPS polymer matrix and G-ZnO nanofiller narrowed the H₂O transmission path; and (3) due to its more hydrophobic surface, water molecules were less likely to enter the interior of PPS/G-ZnO nanocomposites. This study provides valuable insights for developing high-performance PPS-based nanocomposites for various applications.

Recycled duck bones (DBs) and fish shells were processed into natural derivatives. Through innovative design, these natural derivatives were then combined with biopolymers to create a new type of ecofriendly filament suitable for three-dimensional (3D) printing of scaffolds for bone regeneration. The DBs and fish shells were thermally processed to produce DB-derived hydroxyapatite (HA) and fish shell-derived Ca(OH)₂ (TAS), respectively. Poly(ε-caprolactone) (PCL), HA, and TAS were combined and fabricated into new composite filaments, which were then transformed into scaffolds using 3D printing technology. The structure and antibacterial behaviors of the obtained composite scaffolds were studied. Alone, PCL showed no bacterial inhibition. MHA (a mix of HA and TAS) was added to PCL to form a PCL/MHA composite material, which significantly improved the functional properties of PCL and enhanced cell attachment and proliferation. The Ca(OH)₂ content of TAS was responsible for the antibacterial effect. The PCL/MHA composites were porous and displayed enhanced osteoblast proliferation in vitro. The osteoblast cell population do not affected when cultured on the PCL/HA and PCL/MHA series composites according to cell cycle distribution analysis. The surfaces of the various PCL/HA and PCL/MHA composites showed elevated levels of calcium and phosphorus compounds when exposed to simulated body fluids. Calcium and phosphate ions were rapidly deposited on PCL/HA and PCL/MHA composite scaffolds in osteoblasts according to the cell mineralization assay. Our findings suggest great potential of the PCL/HA and PCL/MHA composite scaffolds in bone tissue engineering applications.

Attapulgite (ATT) has never been used as a barrier additive in polypropylene (PP). As a filler, ATT should be added in high content to PP. However, that would result in increased costs. Moreover, the compatibility between ATT and the PP matrix is poor due to the lack of functional groups in PP. In this study, carboxylic groups were introduced to PP to form a modified polypropylene (MPP). ATT was purified, and a low content of it was added to MPP to prepare MPP/ATT nanocomposites. The analysis from FTIR indicated that ATT could react with MPP. According to the results of oxygen and water permeability tests, the barrier performance of the nanocomposite was optimal when the ATT content was 0.4%. This great improvement in barrier performance might be ascribed to the following three reasons: (1) The existence of ATT extended the penetration path of O₂ or H₂O molecules; (2) O₂ or H₂O molecules may be adsorbed and stored in the porous structure of ATT; (3) Most importantly, –COOH of MPP reacted with –OH on the surface of ATT, thereby the inner structure of the nanocomposite was denser, and it was less permeable to molecules. Therefore, nanocomposites prepared by adding ATT to MPP have excellent properties and low cost. They can be used as food packaging materials and for other related applications.