Junwei Fang

Gas channeling phenomena in carbonate fracture-vuggy reservoirs frequently occur, primarily in the form of negative pressure gas channeling and displacement gas channeling, with the possibility of mutual conversion between the two. This is accompanied by the risk of hydrogen sulfide (H₂S) release from the reservoir, which poses significant challenges to controlling safety. Currently, liquid bridging and gel plugging technologies are effective methods for mitigating complex issues such as downhole overflow, fluid loss, and heavy oil backflow. This paper focuses on the development and optimization of key treatment agents, including high-temperature-resistant polymers and crosslinking agents, to formulate a high-temperature chemical gel plugging agent. A gel-breaking, high-strength colloidal chemical gel plugging agent system capable of withstanding temperatures up to 150 °C was developed, and it has an apparent viscosity of about 7500 mPa·s, an energy storage modulus and a loss modulus of 51 Pa and 6 Pa, respectively, after gel formation at elevated temperatures, and an apparent viscosity retention rate of the gel of greater than 82% after aging for 9 d at a temperature of 150 °C. This system forms a stable gas isolation barrier in the wellbore, with performance remaining stable after 7 to 12 days of aging, and the degradation rate reaches 99.8% after 24 h at 150 °C. This technology is of significant importance in solving complex issues such as overflow, fluid loss, and heavy oil backflow in gas injection and recovery wells in high-temperature, high-pressure reservoir conditions.

With the development of oil exploration, the number of complex situations encountered in the drilling process is continuously increasing. During the operation of large displacement and horizontal wells, the safe density window of drilling fluid is narrow in complex formations and the lost circulation problem is becoming increasingly prominent. This can easily cause the drilling fluid to enter the formation from inside the well through lost circulation channels, which will prolong the drilling cycle, increase drilling costs, affect geological logging, and could cause a series of malignant accidents (such as blowout, sticking of a drilling tool, borehole collapse, and well abandoned). According to the severity, common lost circulation can be classified into three types: fractured lost circulation, karst cave lost circulation, and permeability lost circulation. Currently, researchers are developing different types of lost circulation materials (LCMs) for various lost circulation situations. Compared with conventional lost circulation control methods, the polymer gel lost circulation control technique applies a three-dimensional cage-like viscoelastic body formed via the crosslinking reaction of polymer gels. These materials have strong deformability and can enter fractures and holes through extrusion and deformation without being restricted by lost circulation channels. They then settle in the lost circulation formation and form a plugging layer through a curing reaction or swelling effect. Among the polymer gel LCMs, high-temperature resistant polymer gels can either be used alone or in combination with other LCMs, bringing the advantages of adjustable gelation time, strong lost circulation control ability, and strong filtration ability of the plugging slurry. Moreover, they are suitable for the lost circulation control of microporous leaky layer and have limited influence on the performance of drilling fluids. Therefore, the high-temperature resistant polymer gel lost circulation control technique is increasingly becoming a hot spot in the research of LCMs nowadays. This paper summarizes the research progress into high-temperature resistant functional gels for profile control and water shutoff, lost circulation prevention and control, and hydraulic fracturing. Furthermore, the current application status of high-temperature resistant gels and high-temperature resistant gel temporary plugging agents is demonstrated, followed by a detailed overview of the gel-breaking methods. Overall, this research lays the theoretical foundation for the application and promotion of high-temperature resistant gels.