Owing to the melting and healing properties of thermoplastic resin, additive manufacturing or 3D printing is considered one of the most promising technologies for fiber-reinforced thermoplastic composites. However, manufacturing defects are still the main concern, which significantly limits the application of 3D-printed composite structures. To gain an insight into the effects of different processing parameters on the typical manufacturing defects, a micro-scale analysis was carried out via Micro-CT technology on the 3D-printed continuous carbon fiber-reinforced polylactic acid (PLA) composite specimens. The bias distribution of the fiber in the deposited filament was found. Moreover, when the feed rate of the filament was reduced from 100% to 50%, the a/b value was closer to 3.33, but the porosity increased from 7.077% to 25.352%. When the layer thickness was 0.2 mm, the increased nozzle pressure reduced the porosity but also increased the risk of fiber bundle breakage. The research provides an effective approach for analyzing the micro-structure of 3D printed composite structures and thus offers guidance for the processing control.

Ultrasonic welding technology represents an advanced method for joining thermoplastic composites. However, there exists a scarcity of systematic investigations into welding parameters and their influence on the morphological characteristics and quality of the welded regions. Furthermore, a comprehensive experimental understanding of the welded joint failure mechanisms remains deficient. A robust model for simulating the failure behavior of welded joints under loading has yet to be formulated. In this study, ultrasonic welded specimens were fabricated using distinct welding control methods and varied parameter combinations. Diverse experimental methodologies are employed to assess the morphological features of the welded areas, ascertain specimen strength, and observe welding interface failure modes. Based on a cohesive model, a finite element model is developed to predict the strength of the ultrasonic welded joints and elucidate the failure mechanisms. The results showed that, under identical welding parameters, the specimens welded with a high amplitude and low welding force exhibit superior welding quality. The specimens produced under displacement control exhibit minimal dispersion in strength. The proposed finite element model effectively prognosticates both welded joint strength and failure modes.