This study investigated the effects of plasma electrolytic oxidation (PEO) treatment in a Ca- and P-rich electrolyte on the surface of the Ti-6Al-4V alloy with distinct α/β phase proportions previously induced by heat treatments. The results revealed that the α/β phase proportions were successfully altered by the heat treatment temperatures, forming α phase plates surrounded by β phase precipitates. PEO-treated samples exhibited a thick and microsized porous TiO₂ coating in the anatase and rutile crystalline forms. The oxide layer was depleted by Al and V atoms, while Ca and P were gradually enriched along the coatings. Chemical analysis also indicated the absorption of water and organic molecules into the outer layer. PEO-treated samples had microscale roughness and thickness, hydrophilic behavior, and surface energy mainly formed by the dispersive component. The bulk’s elastic modulus decreased with β phase precipitation, while the alloying elements directly influenced the Vickers microhardness. The corrosion tests indicated a stable and protective layer in the PEO-treated samples, showing better corrosion resistance than untreated ones. Overall, the findings indicated that the α and β phase proportion significantly impacts the mechanical properties, while the PEO treatment acts in the corrosion protection and surface aspects, suggesting that combining both approaches could be a powerful tool in biomedical applications.

Due to their lower cost and good mechanical and corrosion properties, ferrous materials such as stainless steel (SS) are commonly used as bio-materials, mainly as surgical instruments and implants. Surface treatments such as plasma electrolytic oxidation (PEO) can be a valuable tool to increase corrosion resistance and enhance the bio-compatibility of metallic materials. In this scenario, the current study evaluated the effect of electrolyte composition on the surface of SS304 submitted to PEO treatment. The variation in the amount of KOH and Ta(OH)₅ promoted significant changes in the surface characteristics, forming Fe-rich oxide plates, Ta-rich agglomerate particles, and an exposed substrate. The PEO-treated substrates were depleted of some alloying elements (Cr, Ni, and Mn), which, allied to the Ta-enrichment, affected the roughness, wettability, phase stability, micro-hardness, and corrosion resistance. All the PEO treatments presented a phase composition of single γ-Fe instead of a dual α + γ phase from the untreated substrate, which was understood in terms of the Ni_eq-Cr_eq diagram. The corrosion tests indicated that the PEO treatment significantly affected the corrosion parameters, having the presence of a non-uniform oxide layer. The findings show that it is possible to control the chemical and phase composition of SS304 material employing PEO treatment.