Yun-Hee Lee

In this study, we investigate the excess volume (VE) of 24 binary miscible and compound alloy melts using electrostatic levitation. Notably, Pd50X50 (X = Fe, Co, and Ni) and Pt50Fe50 solid solutions with slightly negative or zero mixing enthalpy (ΔHmix) display pronounced positive VE and significantly improved liquid stability after alloying, whereas compound alloy liquids with negative ΔHmix exhibit negative VE. Moreover, the VE of Pd50X50 and Pt50X50 consistently decreases with the increasing number of electrons in X, indicating a magneto-volume effect observed in specific heat measurements. These findings suggest that the formation of excess volume is influenced by both magnetic and thermodynamic contributions.

Precise density and thermal expansion measurements of refractory materials are extremely challenging due to the chemical reactions and thermal gradients at ultrahigh temperatures. The UV image technique has been successfully applied to the density measurements at high temperatures above 3000 K. However, intense radiation from the sample can blur the edge of the sample image, leading to uncertain measurements. In this study, we investigate the influence of the contrast between the UV background light and sample radiation (B–S) on density measurements. We find that lower B–S contrast can significantly affect the calibration factor that converts image pixels to real size, resulting in underestimated density with scattering and overestimated thermal expansion coefficients at ultrahigh temperatures. This result underscores the necessity of adequate B–S contrast to ensure the precision of density measurements using UV imaging methods for refractory materials beyond 3000 K. By considering the critical minimum value of the B–S contrast, we successfully measure the densities and thermal expansion coefficients of four refractory metal liquids (tungsten, rhenium, osmium, and tantalum) with the improved UV technique, which are crucial for high-temperature industries. This work will be valuable for other imaging methods measuring the thermophysical properties at ultrahigh temperatures.

The dynamic diamond anvil cell (dDAC) technique has attracted great interest because it possibly provides a bridge between static and dynamic compression studies with fast, repeatable, and controllable compression rates. The dDAC can be a particularly useful tool to study the pathways and kinetics of phase transitions under dynamic pressurization if simultaneous measurements of physical quantities are possible as a function of time. We here report the development of a real-time event monitoring (RTEM) system with dDAC, which can simultaneously record the volume, pressure, optical image, and structure of materials during dynamic compression runs. In particular, the volume measurement using both Fabry–Pérot interferogram and optical images facilitates the construction of an equation of state (EoS) using the dDAC in a home-laboratory. We also developed an in-line ruby pressure measurement (IRPM) system to be deployed at a synchrotron x-ray facility. This system provides simultaneous measurements of pressure and x-ray diffraction in low and narrow pressure ranges. The EoSs of ice VI obtained from the RTEM and the x-ray diffraction data with the IRPM are consistent with each other. The complementarity of both RTEM and IRPM systems will provide a great opportunity to scrutinize the detailed kinetic pathways of phase transitions using dDAC.

We study the effects of Ag addition on thermal stability and thermophysical properties of Ti-Zr-Ni icosahedral quasicrystals. The Ag addition results in increasing the coherence length and thermal stability of the icosahedral phase (i-phase) of the as-cast Ti_35.2Zr_43.8Ni₂₁ alloy, which are maximized at around 4 at.% Ag addition. Differential scanning calorimetry (DSC) and electrostatic levitation (ESL) experiments reveal that the addition suppresses the i-phase decomposition on heating and cooling. We find that considerable amount of the i-phase remains in the samples processed by radiational cooling in ESL as the Ag concentration increases. These results demonstrate that Ag addition stabilizes the i-phase of the Ti_35.2Zr_43.8Ni₂₁ alloy. No anomalous effect of Ag addition is found on density and viscosity of the Ti_35.2Zr_43.8Ni₂₁ liquid.