Xiaofeng Jia

Ti-Al intermetallic compounds (Ti-Al IMCs) are emerging as lightweight, high-temperature structural materials with considerable application potential. Owing to their low density and high-temperature capability, these materials can improve the thrust-to-weight ratio of aeroengines, enhance the high-temperature service performance of aircraft, increase fuel efficiency, and improve adaptability to harsh environments. However, their intrinsic room-temperature brittleness leads to high cutting forces, elevated cutting temperatures, and severe tool wear during machining, making it difficult to ensure machining quality and limiting their large-scale applications in the aerospace industry. Ultrasonic vibration-assisted machining (UVAM) introduces a high-frequency, low-amplitude intermittent cutting mechanism that actively regulates material removal and offers a feasible route for overcoming the machining bottleneck of Ti-Al IMCs. This review summarizes the recent progress in UVAM for machining Ti-Al IMCs. First, the typical applications and machining characteristics of Ti-Al IMCs are discussed. Existing studies are then reviewed in terms of cutting performance, including cutting force, cutting temperature, chip morphology, tool wear, and post-machining surface integrity, including surface roughness, surface defects, residual stress, and work hardening. The reviewed evidence indicates that UVAM can reduce cutting forces and temperatures, improve chip morphology, and extend the tool life. It can also improve machined surface integrity by decreasing surface roughness, suppressing surface defects, inducing beneficial residual compressive stress layers, and regulating work-hardening behavior. This review provides systematic theoretical guidance and technical references for improving the machinability of Ti-Al IMCs via UVAM, thereby enabling the controllable, high-performance, and high-reliability fabrication of these difficult-to-machine materials in aerospace precision manufacturing.

During the drilling process of carbon fiber reinforced polymer (CFRP), defects such as exit delamination, tearing, and burrs are prone to occur, among which excessive axial force during drilling is the main reason for the generation of exit delamination defects. In this study, ultrasonic-assisted and conventional drilling with twist and dagger drills were investigated on 5 mm-thick multi-directional laminated fiber sheets made of T300-12k/AG80 carbon fiber composite with different orientations. The axial force evolutions in each case were monitored when drilling holes in CFRP plates, and the axial force of drilling and the appearance characteristics of hole outlet were compared. The experimental results showed that the ultrasonic assisted drilling reduced the axial drilling forces of twist and dagger drill by up to 20.6% and 30.7%, respectively, compared to conventional drills. In addition, as the feed rate increases, the axial force of drilling gradually increases, and the exit delamination factor shows an overall increasing trend. The ultrasonic vibrations reduced the exit delamination damage of both drills. A special structure of the dagger drill effectively avoided exit delamination during ultrasonic-assisted drilling, which makes the incision more neat to improve the processing quality.

The present work introduces a laser-induced cavitation bubble technique for forming an axisymmetric structure (i.e., microgroove) and the dynamics of a cavitation bubble from initial expansion to the collapse stages that were also simulated. Furthermore, the shock wave signals and dynamic properties of the cavitation bubble were recorded using a hydrophone and a high-speed camera. The experiments on microgrooves formed by laser-induced cavitation bubble stamping were carried out, and the effects of laser energy, the initial position of the bubble, and the number of impacts on the microformability of aluminum sheets are discussed. The depth of the microgroove was investigated using experiments, and it was found that the process can serve as a rapid technique for impressing microfeatures on thin-sheet metals. The experimental results showed that as the initial position of the bubble increased, the deformation depth decreased. As the laser energy and number of impacts increased, the deformation depth increased. The results of the response surface experiments showed that a laser energy of 27 mJ, 3 impacts, and a bubble position of 3 mm were optimal for the process. By using the optimal parameters, flat and smooth microgrooves with a forming depth of 102.54 µm were successfully fabricated. Furthermore, the maximum thickness thinning of the microgroove section occurred at the entrance areas, and this area had the greatest hardness. This also indicated that the greatest amount of plastic deformation of the material and grain refinement occurred in this area. On the other hand, the aluminum foil did not undergo oxidation during the plastic deformation process. These results demonstrated that laser-induced bubble stamping is an advanced micromachining method with promising applications.