This work focuses on the fabrication and evaluation of a passive wireless sensor for the monitoring of the temperature and corrosion of a metal material at high temperatures. An inductor–capacitor (LC) resonator sensor was fabricated through the screen printing of Ag-based inks on dense polycrystalline Al₂O₃ substrates. The LC design was modeled using the ANSYS HFSS modeling package, with the LC passive wireless sensors operating at frequencies from 70 to 100 MHz. The wireless response of the LC was interrogated and received by a radio frequency signal generator and spectrum analyzer at temperatures from 50 to 800 °C in real time. The corrosion kinetics of the Cu 110 was characterized through thermogravimetric (TGA) analysis and microscopy images, and the oxide thickness growth was then correlated to the wireless sensor signal under isothermal conditions at 800 °C. The results showed that the wireless signal was consistent with the corrosion kinetics and temperature, indicating that these two characteristics can be further deconvoluted in the future. In addition, the sensor also showed a magnitude- and frequency-dependent response to crack/spallation events in the oxide corrosion layer, permitting the in situ wireless identification of these catastrophic events on the metal surface at high temperatures.

A passive wireless high-temperature sensor for far-field applications was developed for stable temperature sensing up to 1000 °C. The goal is to leverage the properties of electroceramic materials, including adequate electrical conductivity, high-temperature resilience, and chemical stability in harsh environments. Initial sensors were fabricated using Ag for operation to 600 °C to achieve a baseline understanding of temperature sensing principles using patch antenna designs. Fabrication then followed with higher temperature sensors made from (In, Sn) O₂ (ITO) for evaluation up to 1000 °C. A patch antenna was modeled in ANSYS HFSS to operate in a high-frequency region (2.5–3.5 GHz) within a 50 × 50 mm² confined geometric area using characteristic material properties. The sensor was fabricated on Al₂O₃ using screen printing methods and then sintered at 700 °C for Ag and 1200 °C for ITO in an ambient atmosphere. Sensors were evaluated at 600 °C for Ag and 1000 °C for ITO and analyzed at set interrogating distances up to 0.75 m using ultra-wideband slot antennas to collect scattering parameters. The sensitivity (average change in resonant frequency with respect to temperature) from 50 to 1000 °C was between 22 and 62 kHz/°C which decreased as interrogating distances reached 0.75 m.