The development of an electrochemical dissolved oxygen (DO) sensor based on a novel Cu(II) complex-modified screen printed carbon electrode is reported. The voltammetric behavior of the modified electrode was investigated at different scan rates and oxygen concentrations in PBS (pH = 7). An increase of cathodic current (at about −0.4 vs. Ag/AgCl) with the addition of oxygen was observed. The modified Cu(II) complex electrode was demonstrated for the determination of DO in water using chronoamperometry. A small size and low power consumption home-made portable electrochemical analyzer based on custom electronics for sensor interfacing and operating in voltammetry and amperometry modes has been also designed and fabricated. Its performances in the monitoring of DO in water were compared with a commercial one.

Ag@iron oxide nanocomposite powders were synthesized via a two‐step chemical method. Characterization by UV‐Vis, XRD, SEM‐EDX and TEM revealed they are composed of nanosized crystalline silver particles in strict contact with amorphous iron oxide(s). The electrochemical behavior of the synthesized Ag@iron oxide composite was investigated by cyclic voltammetry. Compared with the single phase‐modified electrodes, the Ag@iron oxide/SPCE electrode exhibits an enhanced cathodic current in response to the target analyte, due to a synergistic effect between Ag crystallites and amorphous iron oxide nanoparticles. An amperometric sensor for detection of nitrate based on Ag@iron oxide modified screen‐printed electrode (Ag@iron oxide/SPCE) has been fabricated, showing a good sensitivity (663 µA mM⁻¹ cm⁻²) and a detection limit of 30 µM.

Ag@α-Fe₂O₃ nanocomposite having a core–shell structure was synthesized by a two-step reduction-sol gel approach, including Ag nanoparticles synthesis by sodium borohydride as the reducing agent in a first step and the subsequent mixing with a Fe⁺³ sol for α-Fe₂O₃ coating. The synthesized Ag@α-Fe₂O₃ nanocomposite has been characterized by various techniques, such as SEM, TEM and UV-Vis spectroscopy. The electrical and gas sensing properties of the synthesized composite towards low concentrations of ethanol have been evaluated. The Ag@α-Fe₂O₃ nanocomposite showed better sensing characteristics than the pure α-Fe₂O₃. The peculiar hierarchical nano-architecture and the chemical and electronic sensitization effect of Ag nanoparticles in Ag@α-Fe₂O₃ sensors were postulated to play a key role in modulating gas-sensing properties in comparison to pristine α-Fe₂O₃ sensors.