Jie Zhu

To solve the problems of poor weld formation, difficult slag removal, and inferior joint microstructure and hardness in conventional narrow-gap submerged arc welding (NG-SAW), a swing arc NG-SAW process assisted by pre-embedding cold wires was proposed. Synergistically optimizing the welding energy parameters and additional cold wires ensured sound weld formation and enhanced slag detachability, while the efficiency of multilayer welding was improved by reducing the number of weld layers by 33.3%. The slag adhesion mechanism is clarified as follows: a high welding heat input facilitates elemental diffusion at the weld–slag interface, leading to the formation of a continuous and thick interlayer composed of (Fe,Mn)O and MgO-Al₂O₃-CaO phases. This interlayer strengthens the chemical bonding between slag and weld, thereby impeding slag removal. Microstructure evolution analysis of the multilayer welded joint revealed that the variable-angle design increases the groove volume and, combined with the heat-absorbing effect of the additional wires, accelerates molten pool cooling, thereby refining grains in both the weld metal zone and reheat-affected zone. Meanwhile, the tempering exerted by the heat-affected zone (HAZ) of the subsequent weld layer on the previous layer is attenuated. This promotes the gradual transformation of hard-brittle lath martensite in the coarse-grained heat-affected zone (CGHAZ) of the bottom layer into tougher tempered martensite/bainite in the CGHAZ of the upper layers. As a result, the hardness uniformity within the HAZ, the critical weak region of the joint, was enhanced by 54%, enabling synchronous improvement in microstructural homogeneity, hardness distribution, and overall welding efficiency.

Brazing a SiO_2f/SiO₂ composite with metals is often faced with two problems: poor wettability with the brazing alloy and high residual stress in the joint. To overcome these problems, we report a combined method of selective etching and depositing reduced graphene oxide (rGO) on the surface of a SiO_2f/SiO₂ composite (3D-rGO-SiO_2f/SiO₂) to assist brazing with TC4. After the combined treatment, a “3D-rGO” buffer layer formed on the surface layer of the SiO_2f/SiO₂, and the contact angle was reduced from 130° to 38°, which meant the wettability of active brazing alloy on the surface of SiO_2f/SiO₂ was obviously improved. In addition, the “3D-rGO” buffer layer contributed to fully integrating the brazing alloy and SiO_2f/SiO₂; then, the infiltration of the brazing alloy into the surface layer of the SiO_2f/SiO₂ was enhanced and formed the reduced graphene oxide with a pinning structure in the three dimensional (“3D-pinning-rGO”) structure. Moreover, the joining area of the brazing alloy and SiO_2f/SiO₂ was expanded and the mismatch degree between the SiO_2f/SiO₂ and TC4 was reduced, which was achieved by the “3D-pinning-rGO” structure. Furthermore, the concentration of the residual stress in the SiO_2f/SiO₂-TC4 joints transferred from the SiO_2f/SiO₂ to the braided quartz fibers, and the residual stress reduced from 142 MPa to 85 MPa. Furthermore, the 3D-pinning-rGO layer facilitated the transfer of heat between the substrates during the brazing process. Finally, the shear strength of the SiO_2f/SiO₂-TC4 joints increased from 12.5 MPa to 43.7 MPa by the selective etching and depositing rGO method.