This study investigated the impact of calcination temperature on the structural properties of CuAl catalyst which was found to be a robust nano-structured catalyst calcined directly without ramping at 400 °C and performed exceedingly well for aqueous phase hydrogenolysis of glycerol. Various samples of CuAl catalysts were prepared by co-precipitation at Cu: Al molar ratio 1:1 and were calcined at different temperatures (300–1000 °C). The obtained catalysts were reduced at 200 °C before their activity testing for glycerol hydrogenolysis reaction. To correlate the structure-activity, the catalysts were thoroughly characterized by XRD, XPS, BET, TEM, H₂-TPR, NH₃-TPD, and pyridine FTIR. It was observed that with an increase in calcination temperature from 300 to 700 °C, the glycerol conversion also increased from 47 to 55% with 93% selectivity to 1,2-PDO. The better performance of these catalysts was mainly related to the predominant presence of Brønsted acid sites, an appropriate ratio of the Cu⁰ to CuAl₂O₄ + CuO (0.33) and CuAl₂O₄ to CuO phases (0.35), the existence of Cu₂O phase and the smaller Cu⁰ particle size. It was shown that altering the ramping rate for the calcination temperature of 400 °C impacted the catalytic activity. The CuAl-400 (DC) (direct calcined) catalyst exhibited a maximum glycerol conversion of 60%.

Current global challenges associated with energy security and climate emergency, caused by the combustion of fossil fuels (e.g., jet fuel and diesel), necessitate the accelerated development and deployment of sustainable fuels derived from renewable biomass-based chemical feedstocks. This study focuses on the production of long-chain (straight and branched) ketones by direct α-alkylation of short chain ketones using both homogenous and solid base catalysts in water. Thus, produced long-chain ketones are fuel precursors and can subsequently be hydrogenated to long-chain alkanes suitable for blending in aviation and liquid transportation fuels. Herein, we report a thorough investigation of the catalytic activity of Pd in combination with, (i) homogenous and solid base additives; (ii) screening of different supports using NaOH as a base additive, and (iii) a comparative study of the Ni and Pd metals supported on layered double oxides (LDOs) in α-alkylation of 2-butanone with 1-propanol as an exemplar process. Among these systems, 5%Pd/BaSO₄ with NaOH as a base showed the best results, giving 94% 2-butanone conversion and 84% selectivity to alkylated ketones. These results demonstrated that both metal and base sites are necessary for the selective conversion of 2-butanone to alkylated ketones. Additionally, amongst the solid base additives, Pd/C with 5% Ba/hydrotalcite showed the best result with 51% 2-butanone conversion and 36% selectivity to the alkylated ketones. Further, the screening of heterogenous acid-base catalysts 2.5%Ni/Ba_1.2Mg₃Al₁ exhibited an adequate catalytic activity (21%) and ketone selectivity (47%).