The integrity of wellbores is essential for the safe and efficient operation of drilling activities. Cement plays a critical role in this process, serving as a primary barrier that isolates the casing from the surrounding formation. To ensure the proper application of cement in wells, a thorough understanding of its mechanical properties is essential. Latex-modified cement stone (LMCS) offers significant advantages due to its anti-channeling, anti-corrosion, and mechanical characteristics. This study examined the mechanical properties of LMCS through uniaxial and triaxial compression and Brazilian splitting tests. Under uniaxial compression, the elastic modulus, Poisson’s ratio, and compressive strength of LMCS were found to range from 4.08 to 8.29 GPa, 0.05 to 0.46, and 15.82 to 22.21 MPa, respectively. In triaxial compression tests with confining pressures of 2 MPa, 4 MPa, 6 MPa, 8 MPa, and 10 MPa, the elastic modulus ranged from 4.48 to 6.87 GPa, Poisson’s ratio from 0.05 to 0.16, and compressive strength from 27.38 to 39.58 MPa. The tensile strength of LMCS ranged from 2.34 to 3.72 MPa. Moreover, the compressive strength of LMCS increased with confining pressure, showing enhanced resistance to failure due to the confining effect. However, the rate of increase gradually diminished. Strength criteria for LMCS, including Mohr–Coulomb and Drucker–Prager parameters, were derived from the triaxial compression tests. These strength criteria parameters provide a useful reference for developing the constitutive model of LMCS and for simulating triaxial compression conditions. The findings of this research offer valuable insights that can guide the construction of oil and gas wells.

During the cyclic injection and extraction process in underground storage wellbores, the cement sheath undergoes loading and unloading stress cycles. In this study, we investigated the mechanical properties of latex-modified cement stone (LMCS), widely used in oil and gas wells, through uniaxial and triaxial cyclic loading and unloading tests. The aim of the study was to determine the effect of various loading conditions on the compressive strength and stress–strain behavior of LMCS. The results show that the stress–strain curve of LMCS exhibits a hysteresis loop phenomenon, with the loop intervals decreasing throughout the entire cyclic loading and unloading process. As the number of cycles increases, the cumulative plastic strain of the LMCS increases approximately linearly. Under uniaxial cyclic loading and unloading conditions, the elastic modulus tends to stabilize. However, under triaxial conditions, the elastic modulus increases continuously as the number of cycles increases. This result provides data for engineering predictions. Furthermore, a comparison of the uniaxial and triaxial cyclic loading and unloading of LMCS shows that its cumulative plastic strain develops rapidly under uniaxial conditions, while the elastic modulus is larger under triaxial conditions. These findings provide a valuable reference for constructing underground storage wellbores.