Xihuai Wang

This study aims to develop an efficient laser cleaning process for removing paint coatings from low-pressure turbine blades while suppressing substrate remelting, focusing on elucidating the underlying paint removal mechanisms on coated aluminum alloy substrates. A pulsed fiber laser (1064 nm, 100 ns) was used to perform single-factor and orthogonal experiments, with laser power (70–100 W), scanning speed (1000–3000 mm/s), and repetition frequency (150–300 kHz) as the main variables. The energy density for each of the 16 orthogonal test samples ranged from 11.9 to 51.0 J/cm². Complete paint removal without substrate damage was achieved within an optimal energy density window of approximately 17–27 J/cm² (e.g., 23.8 J/cm²), whereas higher values above 35 J/cm² (e.g., 35.7 J/cm²) frequently caused localized remelting and pitting. The optimized parameter combination (90 W, 1500 mm/s, 300 kHz) achieved 98% paint removal efficiency in four passes with no observable substrate degradation. Mechanistic analysis indicated that low-to-moderate energy densities promoted interfacial debonding and controlled film ablation, while high energy densities led to substrate melting and reflow. This work clarifies the quantitative correlation between laser parameters, paint removal mechanisms, and remelting suppression, providing a scientific basis for turbine blade maintenance applications.

To address the problem of excessive ablation in conventional laser processing caused by the inhomogeneous energy distribution at the focal point, along with the inherent heterogeneity and surface irregularities of textile materials, a new method for laser printing elastic bandage fabrics was developed. We used flat top light sources, short focal field mirrors, and low power lasers instead of the Gaussian light sources, long focal field mirrors, and high-power lasers used in traditional methods. First, the sample was preheated, and the aspherical lens system was designed and simulated. Then, the physical and chemical properties of laser-processed elastic bandage fabrics were investigated. Finally, based on single-factor experiments, orthogonal experimental analysis was conducted to determine the optimal process parameters. The results show that the optimized optical path can effectively improve the uniformity of the temperature field during laser scanning and enhance focusing performance; as energy gradually accumulates, chemical bonds in polymer molecules break; when the elastic bandage fabric is in a highly elastic state, it exhibits appropriate breaking strength and color difference. The best parameters obtained from the single-factor experiment are as follows: laser power range of 25–34 W, scanning speed range of 2200–2800 mm/s, preheating temperature range of 125–200 °C. The best parameters obtained from the orthogonal experiment are as follows: laser power 28 W, scanning speed 2800 mm/s, and the preheating temperature 175 °C.

Composite coatings reinforced with varying mass fractions of SiC particles were successfully fabricated on 316 stainless steel substrates via laser cladding. The phase compositions, elemental distribution, microstructural characteristics, hardness, wear resistance and corrosion resistance of the composite coatings were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), Vickers hardness testing, friction-wear testing and electrochemical methods. The coatings have no obvious pores, cracks or other defects. The phase compositions of the Hastelloy C276 coating includes γ-(Ni, Fe), Ni₂C, M₆C, M₂(C, N) and M₂₃C₆. SiC addition resulted in the formation of high-hardness phases, such as Cr₃Si and S₅C₃, with their peak intensity increasing with SiC content. The dendrites extend from the bonding zone towards the top of the coatings, and the crystal direction diffuses from the bottom to each area. Compared with the dendritic crystals formed at the bottom, the microstructure at the top is mostly equiaxed crystals and cellular crystals with smaller volume. When SiC powder particles are present around the crystals, the microstructure of the cladding layer grows acicular crystals containing Si and C. These acicular crystals tend to extend away from the residual SiC powder particles, and the grain size in this region is smaller and more densely distributed. This indicates that both melted and unmelted SiC powder particles can contribute to refining the grain structure of the cladding layer. The optimal SiC addition was determined to be 9 wt%, yielding an average microhardness of 670.1 HV_0.5, which is 3.05 times that of the substrate and 1.19 times that of the 0 wt% SiC coating. The wear resistance was significantly enhanced, reflected by a friction coefficient of 0.17 (43.59% of the substrate, 68% of 0 wt%) and a wear rate of 14.32 × 10⁻⁶ mm³N⁻¹·m⁻¹ (27.35% of the substrate, 40.74% of 0 wt%). The self-corrosion potential measured at 315 mV, with a self-corrosion current density of 6.884 × 10⁻⁶ A/cm², and the electrochemical charge-transfer resistance was approximately 25 times that of the substrate and 1.26 times that of the 0 wt%. In this work, SiC-reinforced Hastelloy-SiC composite coating was studied, which provides a new solution to improve the hardness, wear resistance and corrosion resistance of 316L stainless steel.

With the rapid development of integrated circuits, glass substrates are frequently utilized for prototyping various functional electronic circuits due to their superior stability, transparency, and signal integrity. In this experiment, copper wire was printed on a glass substrate using inkjet printing, and the electronic circuit was sintered through laser irradiation with a 532 nm continuous green laser. The relationship between resistivity and microstructure was analyzed after laser sintering at different intensities, scanning speeds, and iterations. The experimental results indicate that the conductivity of the sintered lines initially increases and then decreases with an increase in laser power and scanning speed. At the same power level, multiple sintering runs at a lower scanning speed pose a risk of increased porosity leading to reduced conductivity. Conversely, when the scanning speed exceeds the optimal sintering speed, multiple sintering runs have minimal impact on porosity and conductivity without altering the power.