This study developed a novel material based on polyvinyl alcohol–ethylene glycol (PVA-EG) hydrogel and systematically evaluated its potential application in the removal of animal glue from book surfaces. The microstructure, surface properties, and mechanical characteristics of the PVA-EG hydrogel were analyzed using X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), contact angle measurements, a universal testing machine, and a dynamic mechanical analysis (DMA). The introduction of ethylene glycol (EG) could weaken hydrogen bonding interactions between PVA chains to enhance the molecular chain flexibility of the hydrogel. Notably, the 10% PVA-EG hydrogel shows better crystallinity, higher hydrophilicity, and optimal balance between mechanical strength and flexibility compared to pure PVA, which is conducive to improving the efficiency of the removal of animal glue. Additionally, the effectiveness of the process of removing animal glue was verified by real-time monitoring using europium nitrate at a concentration of 0.4% (w/v) as a fluorescent marker. Such hydrogels with high mechanical properties, strong surface hydrophilicity, good removal efficiency, and gentle treatment characteristics have potential applications in the restoration of cultural heritage.

The presence of harmful oxidizing gases accelerates the oxidation of cellulose fibers in paper, resulting in reduced strength and fading ink. Therefore, the development of highly sensitive NO₂ gas sensors for monitoring and protecting books holds significant practical value. In this manuscript, ZnO/MoS₂ composites were synthesized using sodium molybdate and thiourea as raw materials through a hydrothermal method. The morphology and microstructure were characterized by X-ray diffraction analysis (XRD), energy dispersive spectroscopy (EDS), field emission scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The ZnO/MoS₂ composite exhibited a flower-like structure, with ZnO nanoparticles uniformly attached to the surface of MoS₂, demonstrating advantages such as high specific surface area and good uniformity. The gas sensitivity of the ZnO/MoS₂ nanocomposites reached its peak at 260 °C, with a sensitivity value around 3.5, which represents an improvement compared to pure ZnO, while also enhancing sensitivity. The resistance of the ZnO/MoS₂ gas sensor remained relatively stable in air, exhibiting short response times during transitions between air and NO₂ environments while consistently returning to a stable state. In addition to increasing adsorption capacity and improving light utilization efficiency, the formation of hetero-junctions at the ZnO-MoS₂ interface creates an internal electric field that effectively promotes the rapid separation of photo-generated charge carriers within ZnO, thereby extending carrier lifetime.