While anisotropic extrudate swell in polymer processing is fundamentally driven by physical viscoelastic recovery, this paper proposes a theoretical framework to explicitly isolate and map the purely geometric and kinematic components of this phenomenon. Serving as a mathematical proof-of-concept, a multi-velocity-centre hypothesis is proposed. By introducing a semi-empirical, lumped material-flow calibration parameter, the macroscopic diameter swell ratio is mathematically extended to the discrete local flow field of a rectangular slit die. To evaluate its validity, the analytical framework is subjected to a numerical test for kinematic consistency utilizing isothermal, inelastic power-law fluid CFD simulations, thereby separating geometric mapping from complex viscoelastic stress relaxation. Results indicate that analytical predictions show good agreement with CFD data (error < 5%) strictly within the core zone of high-aspect-ratio dies. However, due to the infinite-slit assumption, 3D flow kinematics near die edges induce velocity decay, leading to local deviations that require future empirical corrections. Although comprehensive physical extrusion experiments and non-isothermal viscoelastic coupling are required for industrial deployment, this semi-empirical kinematic mapping provides a foundational mathematical basis that could potentially inform future inverse die-profile design and shape distortion compensation.

Iron–nickel-based superalloy is an ideal substitute for the expensive Inconel 625 and Inconel 751 alloys. To elucidate the evolution of the microstructure and properties of Ni30 alloy under different thermal treatment conditions, a systematic study was conducted on the microstructural transformation of the alloy’s strengthening γ′ phase following solution treatment and aging, as well prolonged exposure at 750 °C, and the oxidation behavior of the Ni30 alloy was examined. During prolonged thermal exposure, grain growth occurs mainly in the initial stage, and after 200 h, the prolonged exposure time leads to a significant coarsening of γ′ precipitates, whose area fraction increases by more than 10 times compared to their unaged state. After 100 h of aging, the alloy reaches a peak tensile strength of 1270 MPa and a yield strength of 820 MPa; after 2000 h, the alloy maintains a relatively high strength with a slight decrease in ductility. The oxidation kinetic curve of Ni30 alloy follows the quasi-parabolic oxidation law at 750 °C, and its oxidation rate is consistently lower than 0.1 g·m⁻²·h⁻¹ throughout the whole oxidation process, which indicates that it has excellent oxidation resistance. The external oxide layer of Ni30 alloy shows a bilayered structure, and no obvious surface porosity or flaking of oxidation products were observed throughout the high-temperature oxidation test. This study not only contributes to the improvement of material properties, but also promotes innovation and development in the field of high-temperature engineering applications that will help to meet the increasingly stringent requirements of high-temperature working environments.