Peiqing La

Concentrated Solar Power (CSP) technology is advancing toward higher operating temperatures and lower costs: current systems operate at 565 °C, while next-generation systems are targeted to reach 800 °C to overcome efficiency limitations. In this context, low-cost, adaptable molten chloride salts have emerged as ideal heat transfer and thermal energy storage media. Metallic materials are susceptible to performance degradation under such conditions, which not only shortens equipment service life but also entails potential safety hazards. Thus, the development of alloy protection technologies resistant to molten salt corrosion has become an urgent priority for the deployment of next-generation CSP plants. Research has indicated that high-aluminum stainless steel is a promising candidate due to its unique advantages: it can form a stable Al₂O₃ protective film in oxygen-containing anionic environments, effectively inhibiting the dissolution of Cr, Fe, and other elements, and preventing the penetration of corrosive species. Additionally, the incorporation of magnesium-based corrosion inhibitors into MgCl₂-NaCl-KCl ternary molten salt systems has been proven to be an economically viable and efficient corrosion mitigation strategy. This study focused on high-aluminum 310S heat-resistant steel, with its performance validated through targeted experiments: samples subjected to pre-oxidation at 800 °C for 2 h were immersed in a specific ternary molten salt mixture (20.4 wt.% KCl, 55.1 wt.% MgCl₂, 24.5 wt.% NaCl) containing magnesium corrosion inhibitors, followed by a 600 h static corrosion test at 800 °C. The results revealed that the addition of magnesium significantly enhanced the corrosion resistance of high-aluminum 310S. These findings demonstrate that this material holds application potential in the storage tank and pipeline systems of next-generation CSP plants.

In the context of the global energy structure transformation, concentrated solar power (CSP) technology has gained significant attention. Its future trajectory is oriented towards the construction of ultra-high temperature (700–1000 °C) power plants, aiming to enhance thermoelectric conversion efficiency and economic competitiveness. Chloride molten salts, serving as a crucial heat transfer and storage medium in the third-generation CSP system, offer numerous advantages. However, they are highly corrosive to metal materials. This paper provides a comprehensive review of the corrosion behaviors of stainless steels and high-temperature alloys in molten salts. It analyzes the impacts of factors such as temperature and oxygen, and it summarizes various corrosion types, including intergranular corrosion and hot corrosion, along with their underlying mechanisms. Simultaneously, it presents an overview of the types, characteristics, impurity effects, and purification methods of molten salts used for high-temperature heat storage and heat transfer. Moreover, it explores novel technologies such as alternative molten salts, solid particles, gases, liquid metals, and the carbon dioxide Brayton cycle, as well as research directions for improving material performance, like the application of nanoparticles and surface coatings. At present, the corrosion of metal materials in high-temperature molten salts poses a significant bottleneck in the development of CSP. Future research should prioritize the development of commercial alloy materials resistant to chloride molten salt corrosion and conduct in-depth investigations into related influencing factors. This will provide essential support for the advancement of CSP technology.

Concentrated solar power plant (CSP) technology holds significant application value in the renewable energy sector for converting solar radiation into thermal and electrical energy. As a heat storage medium for next-generation solar thermal power stations, chloride salts exhibit strong corrosive effects on structural components. To enhance corrosion resistance of the heated body in molten salt environments, Inconel 625 is modified by incorporating aluminum, which facilitates the formation of a protective oxide film. In this study, High-Aluminum Inconel 625, after cold rolling and solution treatment, was immersed in a NaCl-KCl-MgCl₂ eutectic chloride melt at 650 °C for 200 h. Post-corrosion analysis revealed the formation of an alumina layer on the surface, effectively mitigating corrosion. Increased aluminum content resulted in thicker alumina layers and the formation of oxidation products, such as Cr₂O₃, Fe₂O₃, MoO₂, and MgCr₂O₄ spinel structures, significantly enhancing the alloy’s corrosion resistance. The Inconel 625 cold-rolled plate with 5.31 wt% Al exhibited the best corrosion resistance (3510 μm/year), making it a promising candidate for use in next-generation CSP heat storage and exchange components.