Geopolymers are typically cured either at ambient temperature (~25 °C) or subjected to short-term heat curing before being stored under ambient conditions until testing. However, in hot-arid regions, the daily ambient temperature may exceed 45 °C during summer months. Therefore, such conditions should also be considered as high ambient curing, and their influence on low-calcium geopolymer performance needs to be investigated. In this study, pumice- and fly ash-based geopolymer mortars were produced to evaluate the effects of different curing regimes. In the pumice-based mixtures, 10 wt% of pumice was replaced with metakaolin to enrich the alumina content. Three curing conditions were applied: ambient curing, high ambient curing, and heat curing. Setting times of geopolymers were determined based on each curing regime. Physical properties, including density, water absorption, and sorption coefficient, were assessed. Compressive strength development was evaluated over 90 days. In addition, durability performance was assessed through water resistance, freeze–thaw durability, and resistance against sulphuric and hydrochloric acid. Fourier transform infrared spectroscopy and X-ray diffraction confirmed that geopolymerisation reactions continued significantly up to 90 days under high ambient curing, while mercury intrusion porosimetry showed a reduction in porosity. These findings explain the continuous increase in compressive strength. Pumice-based geopolymers cured under this condition exhibited significantly better long-term strength than those cured under other regimes. High ambient-cured fly ash-based geopolymers, a 3-day strength of 40.3 MPa was achieved, eliminating the need for heat curing. Thus, high ambient curing enables the in situ use of these geopolymers and offers a cost-effective and eco-friendly alternative.