This study investigates the correlation between sintering temperature, microstructure, and mechanical properties in AlSi10Mg alloy produced by supersolidus liquid phase sintering and subsequent artificial aging. Sintering was performed at 571, 575, and 579 °C using different heating rates for a total duration of approximately 5 h, followed by a 2 h dwell at the sintering temperature. At low sintering temperature, the alloy exhibits relatively fine α-Al grains with uniformly distributed Si precipitates, whereas intermediate temperature promotes Si coarsening. At higher temperature, excessive liquid formation leads to coarse α-Al grains and the development of partially interconnected Si networks. β-Al₅FeSi progressively coarsen with increasing sintering temperature. In the as-sintered state, the modest mechanical properties result from coarse α-Al grain size and subgrain structure, as well as from the size, morphology, and distribution of the Si phase. After aging (at 160 °C for 6 h following solution treatment at 530 °C for 30 min), the hardness and UTS were almost double (going from 44 ± 1 to 103 ± 2 HV and from 121 ± 1 to 273 ± 40 MPa). Meanwhile, α-Al grain size and Si morphology remained unchanged and Fe-rich intermetallics partially transformed into the more stable γ-Al₃FeSi₂ phase.

This study investigated the effect of supersolidus liquid-phase sintering conditions on the powder particle bonding and the AlN-phase formation of an AlSi10Mg alloy. Sintering was conducted at temperatures between 550 and 579 °C, with a holding duration of 2 h under a nitrogen atmosphere. The sintering cycles included four heating segments, performed at rates ranging from 0.2 to 5 °C/min for a total of between 5 and 15 h, and a cooling segment performed at two different cooling rates, 0.15 and 5 °C/min, resulting in durations of 12 and 70 h, respectively. Three powder batches exhibiting different particle size distributions were tested. An X-ray diffractometer, optical microscopy, and scanning electron microscopy were used to characterize phase formation and particle bonding. The results show that higher sintering temperatures and faster heating/cooling rates led to a lower fraction of AlN. In contrast, lower sintering temperatures or slow heating promoted the development of a thicker AlN shell around powder particles, inhibiting the bonding of the AlSi10Mg powder and preventing densification via the sintering process. These findings suggest that sintering at temperatures between 570 and 575 °C, with heating and cooling rates of at least 2 °C/min, constitutes a more favorable window for the densification of AlSi10Mg under a nitrogen atmosphere.