Zhigang Gao

Earthen materials are attractive sustainable building solutions due to their low embodied energy and ecological benefits. However, their inherent weaknesses, such as low strength and poor durability, severely restrict modern engineering applications. Traditional physical or chemical modification methods struggle to balance significant improvement in mechanical performance with the preservation of their core sustainable attributes. To overcome this long-standing challenge, this study proposes a paradigm-shifting solution: a prefabricated monolithic lattice–earth composite wall structure. This system abandons the single-material-centered modification approach. Instead, through macroscopic system-level composite design, reinforced concrete lattices and earthen blocks are prefabricated into integral wall panels in a factory. These panels then work collaboratively with the peripheral frame through reliable integral connections. Via quasi-static tests and theoretical analysis on four scaled wall specimens with different design parameters, this study systematically reveals the working mechanism and performance regulation principles of this composite system. The core findings indicate: (1) The system achieves multiple seismic defense lines and a controllable energy dissipation path through a sequential damage mechanism: “earthen material cracking and friction → lattice yielding and energy dissipation → final defense by the frame.” (2) The ratio of the equivalent lateral stiffness of the prefabricated wall panel to the stiffness of the outer frame is a key dimensionless design parameter controlling the failure mode (ductile shear or brittle bending), and the lattice configuration is an effective means to adjust this parameter. (3) Based on tests and an equivalent stiffness model, quantitative design guidelines are proposed, focusing on optimizing lattice density (recommended: 3–4 lattice columns), limiting the aspect ratio (preferably ≤1.5), and ensuring “strong connections.” This study demonstrates that the system, without sacrificing the intrinsic sustainable advantages of earthen materials, successfully endows them with high performance, meeting modern seismic code requirements and potential for prefabricated construction through system integration innovation. It provides a new path with theoretical foundation and practical feasibility to resolve the core contradiction in the modernization of traditional earthen buildings—the incompatibility between ecological attributes and engineering performance. This lays an important foundation for developing next-generation high-performance green building structural systems.

Basalt fiber reinforced polymer (BFRP) is one of the new materials that can be used for making photovoltaic scaffolds, which can effectively solve the problem of the rapid deterioration of complex environmental performance and high maintenance cost of traditional scaffold materials. This paper focuses on the BFRP photovoltaic support in the cold and arid irrigation area of northwest China, carries out the durability test under the action of chloride salt, freeze-thaw cycle, and chloride salt freeze-thaw environment coupling, and it compares and analyzes the degradation law of the mechanical properties of BFRP sheets under different environmental effects. The performance degradation mechanism of BFRP materials under different environmental effects was revealed by SEM scanning electron microscopy and EDS energy spectrum analysis. The main conclusions are as follows: (1) Under the action of chloride salt, the tensile strength, elastic modulus and elongation at break of the specimen decreased by 11.46%, 7.02%, and 10.27%, respectively. Under the freeze-thaw cycle, the tensile strength and elongation at break of the specimen decreased by 9.62% and 6.85%, while the elastic modulus first increased and then decreased, with a maximum decrease of 12.95%. The degradation of mechanical properties is the most serious under the coupling effect of chloride salt and the freeze-thaw environment. The tensile strength, elastic modulus, and elongation at break of the specimens decreased by 25.73%, 9.55%, and 24.81%, respectively. (2) In the chloride environment, the distribution of elements on the surface of the specimen changed, the metal ions of the fibers precipitated, and ‘black spots‘ and corrosion pits appeared. The resin matrix forms ‘sponge-like‘ pores; under the freeze-thaw cycle, the fiber–resin interface cracks and fiber shedding intensifies; under the coupling effect of chloride freeze-thaw, ‘black spots‘, pits, resin holes, and interface cracks increased, and chloride penetration corrosion accelerated.

Basalt fiber-reinforced polymer (BFRP) composites are increasingly utilized in photovoltaic mounting systems due to their excellent mechanical properties and durability. Bolted connections, valued for their simplicity, ease of installation, and effective load transfer, are widely employed for joining composite components. An orthogonal experimental design was adopted to investigate the effects of key parameters—including bolt end distance, number of bolts, bolt material, bolt diameter, preload, and connection length—on the load-bearing performance of three bolted BFRP plate configurations: lap joint (DJ), single lap joint (DP), and double lap joint (SP). Test results showed that the DJ connection exhibited the highest average tensile load capacity, exceeding those of the SP and DP connections by 45.3% and 50.2%, respectively. This superiority is attributed to the DJ specimen’s longer effective shear length and greater number of load-bearing bolts. Conversely, the SP connection demonstrated the largest average peak displacement, with increases of 29.7% and 52.9% compared to the DP and DJ connections. The double-sided constraint in the SP configuration promotes more uniform preload distribution and enhances shear deformation capacity. Orthogonal sensitivity analysis further revealed that the number of bolts and preload magnitude significantly influenced the ultimate tensile load capacity across all connection types. Finally, a calculation model for the tensile load capacity of bolted BFRP connections was established, incorporating a friction decay coefficient (α) and shear strength (τ). This model yields calculated errors under 15% and is applicable to shear slip-dominated failure modes, thereby providing a parametric basis for optimizing the tensile design of bolted BFRP joints.

To enhance the utilization efficiency of coal gangue aggregate, coarse aggregates are chemically modified with 5% sodium silicate solution. The effects of this modification on the compressive strength and microstructural characteristics of concrete are systematically investigated through integrated macro-testing and micro-characterization. By evaluating the compressive performance of modified coal gangue concrete blocks, the optimal mix ratio of each strength grade of blocks is determined. Experimental results indicate that the apparent density, water absorption, and crushing index of the modified coal gangue coarse aggregate exhibit better mechanical properties than the control group. The modified coal gangue coarse aggregate demonstrates improved mechanical performance, with the compressive strength of 28-day concrete showing a 15.3% increase relative to the control group. Furthermore, using a sodium silicate solution effectively enhances the interface transition zone’s performance between coal gangue coarse aggregate and cement mortar, improving the compactness of this interface. The modified coal gangue concrete blocks exhibit higher compressive strength than the original material. When the substitution rate remains constant, the compressive strength of modified coal gangue concrete decreases with increasing water–cement ratio. Similarly, at a constant water–binder ratio, compressive strength decreases with higher modified gangue aggregate replacement. Finally, compressive tests are conducted on masonry constructed with hollow blocks of strength grades MU7.5, MU10, and MU15. Then, a calculation model for the average compressive strength of modified coal gangue concrete hollow block masonry is proposed, providing theoretical support for its engineering application.