Guanjun Fu

Nickel–Aluminum–Bronze (NAB) has gained significant attention in marine applications due to its excellent corrosion resistance and has shown growing potential for laser powder bed fusion (L-PBF) additive manufacturing. However, research on the fabrication of NAB alloys using L-PBF remains relatively limited. In this study, fully dense NAB samples were successfully fabricated through L-PBF process parameter optimization. The microstructural evolution and mechanical properties of both as-built and annealed L-PBF samples were systematically investigated and compared with those of traditionally cast NAB. The results reveal that the as-built L-PBF specimens primarily consist of columnar β′ grains, with the α phase distributed along the grain boundaries and a small amount of κ phase precipitated within the β′ matrix, distinctly different from the cast microstructure characterized by a columnar α-phase matrix with precipitated β′ and κ phases. After annealing at 675 °C for 6 h, the β′ phase in both methods decomposed into α + κ phases, and the original columnar structure in the L-PBF specimens transformed into a dendritic morphology. Compared to the cast samples, the L-PBF-produced NAB alloy exhibited significantly enhanced yield strength, tensile strength, and microhardness, attributable to rapid solidification during the L-PBF process. Following annealing, the yield strength and elongation increased by 12.8% and 184.4%, respectively, compared to the as-built condition, resulting from the decomposition of the martensitic phase into α + κ phases and further grain refinement.

Particle-based 3D printing shows great potential in high-performance composite fabrication due to high raw material utilization and flexible material compatibility. However, constrained by conventional extrusion system structures, critical issues (non-uniform melt conveying, insufficient mixing efficacy, poor extrusion stability, etc.) remain. To address these, this study proposes a novel separate-type pin screw integrating solid–liquid separation (from split screws) and high-efficiency mixing (from pin screws) to improve CF/PLA composite extrusion efficiency and mixing homogeneity in particle-based 3D printing. Three-dimensional modeling, static strength/stiffness analysis, and POLYFLOW-based numerical simulation of particle melt conveying/mixing in the screw channel were conducted to analyze structural parameter effects on pressure field, shear rate, and mixing. Experiments assessed printer extrusion rate (different screws) and printed specimen mechanical properties. The simulation and experiment confirmed the optimized screw has better pressure distribution and mixing at 20 rpm, with optimal pin parameters: diameter 2 mm, height 1.6 mm, radial angle 60°, and axial spacing 10 mm. This work offers theoretical/structural support for particle-based 3D printing extrusion system optimization.