Wei Li

Solar energy, as a clean and renewable resource, plays a pivotal role in advancing sustainable energy technologies. The efficiency of front-side silver paste is critical for the photovoltaic performance of Tunnel Oxide Passivated Contact (TOPCon) solar cells. In this study, we comprehensively investigated how the composition of organic vehicles in conductive pastes influences both printing rheological properties and electrical performance. Through rheological characterization, contact angle measurements, and Three-Interval Thixotropy Tests (3ITT), we examined the effects of varying solvent, binder, and thixotropic agent ratios on paste properties. The optimized formulation—a solvent mixture of lauryl alcohol ester (TE), butyl carbitol (DGME), butyl carbitol acetate (BCA), and dibutyl phthalate (DBP) in a 3:4:2:1 ratio, with ethyl cellulose (EC) STD10 as the binder and a polyamide wax (PAW)–hydrogenated castor oil (HCO) thixotropic agent at a 3:1 mass ratio—demonstrated superior viscosity control and rapid structural recovery. Printed grid lines achieved a height-to-width ratio (H/W) of 0.35 and a sheet resistance (Rs) of 1.43 Ω/□. These findings reveal direct relationships between organic vehicle composition, paste rheology, and functional performance, providing practical guidance for the design and optimization of high-performance conductive pastes for c-Si solar cells. This work establishes a foundation for improving both the efficiency and reliability of next-generation silver paste formulations in photovoltaic applications.

This study focused on the flexible Ag/AgCl biomedical electrode fabricated by screen printing. It systematically investigated the influence of the Ag/AgCl paste on its performance. By adjusting the type of silver powder and the mass ratio of Ag to AgCl, multiple groups of Ag/AgCl pastes were prepared, and their conductivity, microstructure, electrochemical properties, and mechanical stability were systematically characterized. The research results indicated that the specific surface area of the silver powder and the ratio of Ag to AgCl significantly affected the resistivity of the paste and the interface structure of the electrode. When using high specific surface area sheet-like silver powder H and an Ag:AgCl ratio of 5:5, the prepared electrode exhibited the best comprehensive performance: a lower resistivity (2.16 × 10⁻⁷ Ω·m), stable open-circuit voltage, good redox reversibility, and an impedance lower than that of commercial electrocardiogram electrodes. Further verification through an electrocardiogram detection system confirmed that this electrode could clearly and stably collect human electrocardiogram signals, meeting the practical requirements of electrocardiogram detection. This study provided an important theoretical and experimental basis for the development of high-performance and low-cost screen-printed Ag/AgCl flexible electrodes.

Context Traditional conductive adhesives based on epoxy resin system often encounter problems such as high brittleness and low heat resistance. Therefore, it is particularly important to improve the thermal and mechanical properties of the conductive adhesive. In this study, the effects of SWCNT-Ag and SWCNT fillers on the thermal properties of DGEBA/DETA/Ag conductive adhesive system were studied by using molecular dynamics to construct different cross-linking models. The final results show that the addition of SWCNT and SWCNT-Ag can significantly improve the thermal properties of the conductive adhesive. However, the nanosilver particles on the surface of SWCNT-Ag act as a bridge for the connection between SWCNT and Ag in the conductive adhesive. Therefore, SWCNT-Ag has a more positive impact on the thermal properties of DGEBA/DETA/Ag conductive adhesive system. Methods In this paper, the influence of SWCNT-Ag on the thermal properties of traditional DGEBA/DETA/Ag conductive adhesive system was studied by using Materials Studio software. The volume shrinkage, glass transition temperature, thermal expansion coefficient, and thermal conductivity of the material were calculated based on COMPASS force field. The thermal conductivity is calculated by using reverse non-equilibrium molecular dynamics method. Finally, it is found that SWCNT-Ag has a positive effect on the thermal properties of the conductive adhesive system by comparing several groups of calculation data.

Silver powder, as the primary component of solar silver paste, significantly influences various aspects of the paste’s performance, including printing, sintering, and conductivity. This study reveals that, beyond the shape and size of the silver powders, their microstructure is a critical factor influencing the performance of both silver powders and silver pastes in solar cell applications. The growth process leads to the formation of either polycrystalline aggregated silver powder or crystal growth silver powder. Analyzing the performance characteristics of these different microstructures provides guidance for selecting silver powders for silver pastes at different sintering temperatures. Polycrystalline aggregated silver powder exhibits higher sintering activity, with a sintering initiation temperature around 450 °C. The resulting silver paste, sintered at 750 °C, demonstrates a low sheet resistance of 2.92 mΩ/sq and high adhesion of 2.13 N. This silver powder is suitable for formulating silver pastes with lower sintering temperatures. The solar cell electrode grid lines have a high aspect ratio of 0.37, showing poor uniformity. However, due to the high sintering activity of the silver powder, the glass layer dissolves and deposits more silver, resulting in excellent conductivity, a low contact resistance of the silver electrode, a low series resistance of the solar cell of 1.23 mΩ, and a high photoelectric conversion efficiency of 23.16%. Crystal growth silver powder exhibits the highest tap density of 5.52 g/cm³. The corresponding silver paste shows improved densification upon sintering, especially at 840 °C, yielding a sheet resistance of 2.56 mΩ/sq and adhesion of 3.05 N. This silver powder is suitable for formulating silver pastes with higher sintering temperatures. The solar cell electrode grid lines are uniform with the highest aspect ratio of 0.40, resulting in a smaller shading area, a high fill factor of 81.59%, and a slightly higher photoelectric conversion efficiency of 23.17% compared to the polycrystalline aggregated silver powder.

Silver powder, as the primary component of solar silver paste, significantly influences various aspects of paste performance, including printing, sintering, and conductivity. Silver powders prepared using the liquid-phase reduction method exhibit different microstructures depending on whether the growth process is dominated by aggregation or crystalline growth. This study explores the impact of different silver powder microstructures on packing density and sintering activity. It is observed that polycrystalline aggregated silver powder possesses higher surface energy, lower packing density, and greater sintering activity. Investigation into the influence of different silver powders on the electrical conductivity, adhesion, and structural density of silver paste reveals that polycrystalline aggregated silver powder is more suitable for lower sintering temperature pastes, whereas crystalline growth-type silver powder is better suited for higher sintering temperature pastes, resulting in a denser sintered silver layer. Finally, an analysis of the impact of various silver powders on the aspect ratio and electrical performance of solar cell silver grid lines yields higher aspect ratios (0.40) and photoelectric conversion efficiency (19.26%).

The agglomeration trend of nanosilica particles was found to significantly affect the properties of cement-based materials. The influence of nanosilica suspension on the fluidity, setting time, and compressive strength of cement-based grouts were studied. The hardened pastes were characterized by thermogravimetric (TG) analysis and scanning electron microscopy (SEM). The results showed that the fluidity of cement-based grouts with nanosilica suspension had obviously improved. The setting time was obviously decreased, compared with the reference sample. The compressive strengths for 1 day, 3 days, and 28 days were 12.8%, 14.3%, and 10.1% higher than that of the reference group, respectively. This paper may provide a novel route to improve the mechanical properties of cement-based materials without affecting their workability.

Optimizing the performance of front silver paste is of great significance in improving the efficiency of the photoelectric conversion of crystalline silicon solar cells. As a conductive functional phase of silver paste, the structure and performance of silver powder have an important influence on the sintering process of silver paste and the conductivity of silver electrodes. Because of their two−dimensional structure, flake silver powders can effectively increase the contact area with other silver powders and silicon cells before sintering. Additionally, flake silver particles have higher surface energy and sintering activity than spherical silver particles of the same particle size. However, recent research has mainly focused on the influence of the particle size of silver powder. This paper fills the research gap regarding the morphology of silver powders and clarifies the influence of flake silver powders on the performance of silver paste. The influence of the ratio of spherical silver powder to flake silver powder in silver paste on the sheet resistance, adhesion, and specific contact resistivity of silver film after sintering at 800 °C was studied, and the optimal ratio was determined according to a cross−sectional contact picture of the silver film. The results showed that with the increase in the mass fraction of the flake silver powder, the sheet resistance of the sintered silver film gradually increased, the adhesion first increased and then decreased, and the specific contact resistance first decreased and then increased. When the flake silver powder content was 0%, the minimum sheet resistance of the silver film was 2.41 m Ω/☐. When the flake silver powder content was 30%, the maximum adhesion of the silver film was 6.07 N. When the flake silver powder content was 50%, the minimum specific contact resistivity of the silver film was 0.25 Ω·cm². In conclusion, when the flake silver powder content was 30%, the comprehensive performance of the silver film was the best.

Iron droplet that entrapped in the refining slag reduces the yield of iron, so it is necessary to accurately estimate the settling rate of iron particle in the slag. However, since slag is a solid-liquid coexisting fluid, the sedimentation rate of iron particle cannot be derived even using the Stokes’ equation based on the viscosity of the liquid phase. In this study, using silicone oil in which polyethylene particles were suspended as a slag substitute sample, the sedimentation rate of stainless steel balls was measured, and the apparent viscosity was derived with the Stokes method. The effects of the viscosity of the silicone oil, the solid phase ratio, and the diameter of the metal balls on this apparent viscosity were investigated. It was confirmed that the apparent viscosity changes depending on the diameter of the descending metal balls.