Ryan Heldt

Silicon carbide (SiC) passive thermometry has emerged as a promising post-irradiation examination (PIE) technique for estimating irradiation temperature near the end of irradiation. While dilatometry techniques have been traditionally used to analyze prismatic samples after irradiation, Raman spectroscopy has recently been shown to provide comparable results by analyzing Raman-active phonon modes. In this work, Raman spectroscopy has been applied to the SiC layer of cross-sectioned irradiation tristructural isotropic (TRISO) particles from the AGR-5/6/7 experiment to evaluate the feasibility of particle-scale passive thermometry. Two-dimensional Raman mapping was used to measure the position of the SiC longitudinal optical (LO) phonon, which was then converted to an apparent irradiation temperature using a previously established empirical correlation. Particles from AGR-5/6/7 Compacts 2-2-1 and 5-1-3 were selected as their calculated time-averaged, volume-averaged (TAVA) temperatures (828°C and 706°C, respectively) fall within the range of the sensitivity of the experimental approach. The use of SiC thermometry was anticipated to confirm or highlight potential deviations from calculated end-of-life TAVA temperature across compacts. Four particles from Compact 2-2-1 and two particles from Compact 5-1-3 were selected based on 110mAg inventory (either some measurable activity or below the minimum detection limit) which is commonly used as an indicator of in-pile temperature variation of particles within the same compact. Across every particle selected it was determined that the average LO peak position was located around 968 cm-1 to 969 cm-1. Using the previously determined empirical correlation, this corresponds to an irradiation temperature around 950°C to 966°C, which does not align with the reported TAVA temperature values. This discrepancy in apparent irradiation temperatures likely reflects a combination of uncertainties in the calculated particle temperatures and differences in irradiation history between the present specimens and those used to establish the empirical Raman calibration such as neutron flux (damage rate) and SiC microstructure (as fabricated and irradiated).