Achieving 2.2 GPa Ultra-High Strength in Low-Alloy Steel Using a Direct Quenching and Partitioning Process
Open Access
Abstract
Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) was developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) were comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibited a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at −20 °C. In contrast, the HR-QT steel exhibited tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consisted of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reached 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared with the HR-QT process, the TMCP-DQP process resulted in a finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieved the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilized the RA through carbon enrichment, while the relaxation stage reduced a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminated internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.Keywords
All Related Versions
Funding Information
- National Natural Science Foundation of China (52304389, 2022M720402, A18B1b0061, M22K5a0045)
- China Postdoctoral Science Foundation (52304389, 2022M720402, A18B1b0061, M22K5a0045)
- Structural Metal Alloy Program (SMAP) (52304389, 2022M720402, A18B1b0061, M22K5a0045)
- Multi-Material Net-Shape Parts with Heterogeneous Properties (MMNH) (52304389, 2022M720402, A18B1b0061, M22K5a0045)
This publication has 43 references indexed in Scilit:
- Effect of Nb addition on the microstructure and mechanical properties of an 1800MPa ultrahigh strength steelMaterials Science and Engineering: A, 2015
- Influence of metastable retained austenite on macro and micromechanical properties of steel processed by the Q&P processJournal of Alloys and Compounds, 2014
- Effect of partitioning procedure on microstructure and mechanical properties of a hot-rolled directly quenched and partitioned steelMaterials Science and Engineering: A, 2014
- Characterization of individual retained austenite grains and their stability in low-alloyed TRIP steelsActa Materialia, 2007
- Carbon Diffusion Measurement in Austenite in the Temperature Range 500 °C to 900 °CMetallurgical and Materials Transactions A, 2007
- A study of the carbon distribution in retained austeniteScripta Materialia, 2007
- Carbon partitioning into austenite after martensite transformationActa Materialia, 2003
- Retained Austenite Characteristics and Tensile Properties in a TRIP Type Bainitic Sheet Steel.ISIJ International, 2000
- Influence of rolling of TRIP steel in the intercritical region on the stability of retained austeniteJournal of Materials Processing Technology, 1999
- Effects of Volume Fraction and Stability of Retained Austenite on Ductility of TRIP-aided Dual-phase Steels.ISIJ International, 1992