Na Gong

The effects of austenitizing and austempering temperatures on the bainite transformation kinetics and the microstructural and mechanical properties of a medium-carbon high-silicon ultra-fine bainitic steel were investigated via dilatometric measurements, microstructural characterization and mechanical tests. It is demonstrated that the optimum austenitizing temperature exists for 0.3 wt.%C ultra-fine bainitic steel. Although the finer austenite grain at 950 °C provides more bainite nuclei site and form finer bainitic ferrite plates, the lower dislocation density in plates and the higher volume fraction of the retained austenite reduces the strength and impact toughness of ultra-fine steel. When the austenitizing temperature exceeds 1000 °C, the true thickness of bainitic ferrite plates and the volume fraction of blocky retained austenite in the bainite microstructure increase significantly with the increases in austenitizing temperature, which do harm to the plasticity and impact toughness. The effect of austempering temperature on the transformation behavior and microstructural morphology of ultra-fine bainite is greater than that of austenitizing temperature. The prior martensite, formed when the austempering temperature below Ms, can refine the bainitic ferrite plates and improve the strength and impact toughness. However, the presence of prior martensite divides the untransformed austenite and inhibits the growth of bainite sheaves, thus prolonging the finishing time of bainite transformation. In addition, prior martensite also strengthens the stability of untransformed austenite though carbon partition and enhances the volume fraction of blocky retained austenite, which reduces the plasticity of ultra-fine bainitic steel. According to the experimental results, the optimum austempering process for 0.3 wt. %C ultra-fine bainitic steel is through austenitization at 1000 °C and austempering at 340 °C.

Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) was developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) were comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibited a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at −20 °C. In contrast, the HR-QT steel exhibited tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consisted of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reached 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared with the HR-QT process, the TMCP-DQP process resulted in a finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieved the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilized the RA through carbon enrichment, while the relaxation stage reduced a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminated internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) is developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) are comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibits a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at -20 ℃. In contrast, the HR-QT steel exhibits tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consists of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reaches 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared to the HR-QT process, the TMCP-DQP process results in finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieves the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilizes the RA through carbon enrichment, while the relaxation stage reduces a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminates internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.