Study on Annealing Process of Aluminum Oxide Passivation Layer for PERC Solar Cells
Open Access
Abstract
In this study, Atomic Layer Deposition (ALD) equipment was used to deposit Al2O3 film on a p-type silicon wafer, trimethylaluminum (TMA) and H2O were used as precursor materials, and then the post-annealing process was conducted under atmospheric pressure. The Al2O3 films annealed at different temperatures between 200–500 °C were compared to ascertain the effect of passivation films and to confirm the changes in film structure and thickness before and after annealing through TEM images. Furthermore, the negative fixed charge and interface defect density were analyzed using the C-V measurement method. Photo-induced carrier generation was used to measure the effective minority carrier lifetime, the implied open-circuit voltage, and the effective surface recombination velocity of the film. The carrier lifetime was found to be the longest (2181.7 μs) for Al2O3/Si post-annealed at 400 °C. Finally, with the use of VHF (40.68 MHz) plasma-enhanced chemical vapor deposition (PECVD) equipment, a silicon nitride (SiNx) film was plated as an anti-reflection layer over the front side of the wafer and as a capping layer on the back to realize a passivated emitter and rear contact (PERC) solar cell with optimal efficiency up to 21.54%.Keywords
This publication has 33 references indexed in Scilit:
- Impact of Forming Gas Annealing and Firing on the Al2O3/p-Si Interface State SpectrumElectrochemical and Solid-State Letters, 2011
- Influence of the Deposition Temperature on the c-Si Surface Passivation by Al[sub 2]O[sub 3] Films Synthesized by ALD and PECVDElectrochemical and Solid-State Letters, 2010
- Very low surface recombination velocity on p-type c-Si by high-rate plasma-deposited aluminum oxideApplied Physics Letters, 2009
- High Efficiency Silicon Solar Cells with Bilayer Passivation StructureElectrochemical and Solid-State Letters, 2009
- Negative charge and charging dynamics in Al2O3 films on Si characterized by second-harmonic generationJournal of Applied Physics, 2008
- Very low surface recombination velocities on p-type silicon wafers passivated with a dielectric with fixed negative chargeSolar Energy Materials and Solar Cells, 2006
- Influence of single and double deposition temperatures on the interface quality of atomic layer deposited Al2O3 dielectric thin films on siliconJournal of Applied Physics, 2006
- Surface chemistry of atomic layer deposition: A case study for the trimethylaluminum/water processJournal of Applied Physics, 2005
- Low-Temperature Al2O3 Atomic Layer DepositionChemistry of Materials, 2004
- High rate deposition of a-Si:H and a-SiNx:H by VHF PECVDVacuum, 1998