Laser-Based Powder Bed Fusion of Copper Powder on Aluminum Nitride Ceramics for Power Electronic Applications
Open Access
Abstract
As power electronic modules are increasingly required to provide improved heat dissipation, aluminum nitride (AlN) stands out against other ceramic materials. At the same time, more cost-efficient production of customized products demands shorter development cycles and innovative manufacturing processes. Conventional process chains in power electronics are usually long and inflexible; thus, innovative ways to reduce process steps and faster prototyping are needed. Therefore, this study investigates the usage of additive manufacturing technology—laser-based powder bed fusion of metal powder (PBF-LB/M)—namely copper (Cu), on AlN substrates for power electronic applications. It is found that specific electrical conductivity values can be achieved up to 31 MS/m, and adhesion measured by shear testing reaches 15 MPa. In reliability testing, the newly produced samples exhibit a 25% decrease in adhesion after 250 cycles, which is comparatively moderate. This study shows the feasibility of PBF-LB/M of Cu powder on AlN, emphasizing its strengths and highlighting remaining weaknesses.Keywords
Funding Information
- German Aerospace Center (DLR) (01IF22835N)
This publication has 29 references indexed in Scilit:
- Fabrication of 3D metal-ceramic (Al-AlN) architectures using laser-powder bed fusion processAdditive Manufacturing, 2021
- Influence of selective laser melting process parameters on texture evolution in pure copperJournal of Materials Processing Technology, 2019
- Comparative studies on microstructures, strengths and reliabilities of two types of AlN direct bonding copper substratesCeramics International, 2018
- Selective laser melting of pure Cu with a 1 kW single mode fiber laserProcedia CIRP, 2018
- Selective Laser Melting of Pure CopperJOM, 2017
- Oxidation mechanism of aluminum nitride revisitedJournal of Advanced Ceramics, 2017
- Microstructural studies and bonding strength of pressureless sintered nano-silver joints on silver, direct bond copper (DBC) and copper substrates aged at 300 °CJournal of Alloys and Compounds, 2016
- DBC Technology for Low Cost Power Electronic Substrate ManufacturingProcedia Engineering, 2014
- Reliability of AlN substrates and their solder joints in IGBT power modulesMicroelectronics Reliability, 1999
- Sintered aluminum nitride ceramics for high-power electronic applicationsJOM, 1998