Effect of Grain Orientation on Microstructure and Mechanical Properties of FeCoCrNi High-Entropy Alloy Produced via Laser Melting Deposition

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The long, straight grain boundary of the high-entropy alloy (HEA) produced via laser melting deposition (LMD) is prone to cracking due to unidirectional scanning (single wall). To enhance the competitive growth of columnar grains and improve the overall performance of the alloy, a vertical cross scanning method was employed to fabricate FeCoCrNi HEA (bulk). The influence of grain orientation on the microstructure and mechanical properties of FeCoCrNi-LMD was systematically investigated. Microhardness tests and tensile tests were conducted to assess the mechanical property differences between the single-wall and bulk samples. This study shows that using a single scanning strategy results in monolayer wall grains sized at 129.40 μm, with a max texture strength of 21.29. Employing orthogonal scanning yields 61.15 μm block-like grains with a max texture strength of 11.12. Dislocation densities are 1.084 × 1012 m−2 and 1.156 × 1012 m−2, with average Schmid factors of 0.471 and 0.416. In comparison to the FeCoCrNi-LMD single wall, the bulk material produced through cross-layer orthogonal scanning exhibited reduced residual stress, weakened anisotropy, and improved mechanical properties. These findings are expected to enhance the potential applications of FeCoCrNi-LMD in various industries.
Funding Information
  • National Natural Science Foundation of China (52205409, 22YDTPJC00310)
  • Enterprise Science and Technology Commissioner Project (52205409, 22YDTPJC00310)

This publication has 38 references indexed in Scilit: