A Quick Thickness Measurement Method for Ti-Alloy Sheets Based on a Novel Low-Frequency Phase Feature Model in Eddy Current Testing

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Titanium (Ti) alloy sheets are important mechanical and structural components. However, thickness deviations may occur during the production of Ti-alloy sheets, significantly compromising product quality and structural safety. Eddy current testing (ECT) is a common method for measuring the thickness deviation of metal sheets. Nevertheless, conventional ECT methods often rely on complex calibration procedures or iterative inversion algorithms, thereby limiting their applicability. It was found that when low-frequency ECT excitation is used, such that the eddy current penetration depth exceeds three times the maximum target thickness of the Ti-alloy sheet, the tangent of the ECT coil impedance phase exhibits a linear relationship with the thickness. Based on this observation, by analyzing the low-frequency ECT response of Ti-alloys and separating the real and imaginary parts of the impedance under approximate conditions, a phase feature model was developed. The model effectively describes the linear dependence of the phase tangent on the thickness of the Ti-alloy sheet, offering a succinct characterization. The measurement method based on this model thereby allows for direct thickness calculation from the measured coil impedance without requiring master-curve calibration or iterative computation. Experiments were conducted using a custom-designed ECT coil and impedance analyzer to measure different Ti-alloy specimens. The results indicate that the measurement error was less than 3.5%. This research provides a theoretical foundation as well as a straightforward engineering solution for online, high-speed thickness measurement of Ti-alloy sheets.
Funding Information
  • National Natural Science Foundation of China (62203195)
  • Yunnan Xingdian Talents Support Plan Project (XDYC-QNRC-2023-0030)

This publication has 31 references indexed in Scilit: