Synthesis and characterization of electron beam irradiation-induced damage in polycrystalline metal thin films

Authors:
Publisher website
Google Scholar
Abstract
High-energy physics research, industrial sterilizing, and material processing depend extensively on electron beam accelerators. Exit windows are crucial components of such electron accelerator systems, maintaining vacuum integrity inside the machine while providing mechanical strength, thermal stability, and radiation resistance at the beam-target interface. In this study, thin metallic films of Ni, Ti, Cr, and V were explored for use in electron beam exit windows, and their properties were compared with the properties of their bulk counterparts. Simulation results of metal foils predicted Ti to exhibit less beam power dissipation compared to Ni. However, Ni possesses superior mechanical and structural properties compared to Ti. The performance of these films under electron beam irradiation was examined by depositing thin layers of these films on silicon and metallic substrates using magnetron sputtering and exposing them to e-beam irradiation in a controlled setup. The deposited films were subjected to a dose of approximately 66 kGy at a beam energy of 10 MeV and characterized prior to and postexposure to the beam using field emission scanning electron microscopy, atomic force microscopy, x-ray diffraction (XRD), and nanoindentation. Particular emphasis was given to characteristics like the grain structure, surface morphology, dislocation density, and hardness. XRD patterns revealed irradiation-induced changes in peak intensities, while the crystallinity remained largely unchanged. Nanoindentation results showed that the pristine and irradiated Ti and Ni films were twice as hard when compared to bulk Ti and Ni samples, regardless of the substrate type used (Si or bulk Ti, or Ni). These results emphasize the superior mechanical properties of thin metal films compared to their bulk counterparts. This study advances the optimization of thin film materials for robust and efficient e-beam applications, ensuring improved durability and operational reliability.
Funding Information
  • U.S. Department of Energy (DE-SC-0002286 & SC-0022286)

This publication has 29 references indexed in Scilit: