Plasma Bombardment-Induced Amorphization of (TiNbZrCr)Nx High-Entropy Alloy Nitride Films

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The (TiNbZrCr)Nx high-entropy nitride films (HENFs) were prepared by high-power pulsed magnetron sputtering (HPPMS). The effect of the N2 flow rate (FN) on the HPPMS plasma discharge, film composition, microstructure, residual stress, tribological properties, and corrosion resistance was investigated. Results show that, with the increase in FN, plasma discharge is enhanced. Firstly, the introduced N atoms react with Ti, Nb, Cr, and Zr to form an FCC nitride phase structure. Then, with the increase in plasma bombardment on the deposited film, the HENFs undergo amorphization to form an FCC+ amorphous structure, accompanied by a decrease in grain size and a change in the preferred orientation from (1 1 1) to (2 0 0). The HENFs deposited at FN = 8 sccm show the highest hardness of 27.8 GPa. The HENFs deposited at FN = 12 sccm present the best tribological properties, with a low wear rate of 4.0 × 10−6 mm3N−1m−1. The corrosion resistance of the (TiNbZrCr)Nx HENFs shows a strong correlation with the amorphous phase. The corrosion resistance of the FCC nitride film is the worst, and the corrosion resistance gradually increases with the amorphous transformation of the film. Based on the above results, nanocomposite high-entropy films can be prepared using HPPMS technology and exhibit excellent, comprehensive performance.
Funding Information
  • National Natural Science Foundation of China (51975564, 52375206, 2022065, 2023YFG0246, S202314389094)
  • Science and Technology Department of Sichuan Province (51975564, 52375206, 2022065, 2023YFG0246, S202314389094)
  • Sichuan College Student Innovation Training Program (51975564, 52375206, 2022065, 2023YFG0246, S202314389094)

This publication has 35 references indexed in Scilit: