Carbon in GaN as a nonradiative recombination center

Authors:
Publisher website
Google Scholar
Abstract
Trap-assisted nonradiative recombination has been shown to limit the efficiency of optoelectronic devices. While substitutional carbon (CN) has been suggested to be a nonradiative recombination center in GaN devices, a complete recombination cycle including the two charge-state transition levels has not been previously described. In this work, we investigate the trap-assisted recombination process due to CN in GaN, including multiphonon emission, radiative recombination, trap-assisted Auger–Meitner (TAAM) recombination as well as thermal emission of holes. Our study shows the key role of TAAM processes at the high carrier densities relevant for devices. We also reveal the carrier-density regimes where thermal emission and radiative recombination are expected to play an observable role. Our results highlight that carbon concentrations exceeding ∼1017 cm−3 can have a noticeable impact on device efficiency, not just in GaN active layers but also in InGaN and AlGaN. Our comprehensive formalism not only offers detailed results for carbon but also provides a general framework for assessing the multiple processes that participate in trap-assisted recombination in semiconductors.
Funding Information
  • U.S. Department of Energy (DE-SC0010689)
  • California NanoSystems Institute (Elings Prize Fellowship)
  • Alexander von Humboldt-Stiftung (Humboldt Research Fellowship)
  • Office of Naval Research (N00014-22-1-2808)
  • National Energy Research Scientific Computing Center (BES-ERCAP0021024)

This publication has 41 references indexed in Scilit: