Hot Deformation Behavior and Microstructure Evolution Mechanisms of Ti6Al4V Alloy under Hot Stamping Conditions
Open Access
Abstract
Through the study of the thermal rheological behavior of Ti6Al4V alloy at different temperatures (500 °C, 600 °C, 700 °C, and 800 °C) and different strain rates (0.1 s−1, 0.05 s−1, 0.01 s−1, and 0.005 s−1), a constitutive model was developed for Ti6Al4V alloy across a wide temperature range in the hot stamping process. The model’s correlation coefficient reached 0.9847, indicating its high predictive accuracy. Hot processing maps suitable for the hot stamping process of Ti6Al4V alloy were developed, demonstrating the significant impact of the strain rate on the hot formability of Ti6Al4V alloy. At higher strain rates (>0.05 s−1), the hot processing of Ti6Al4V alloy is less prone to instability. Combining hot processing maps with hot stamping experiments, it was found that the forming quality and thickness uniformity of parts improved significantly with the increase in stamping speed. The phase composition and microstructures of the forming parts under different heating temperature conditions have been investigated using SEM, EBSD, XRD, and TEM, and the maximum heating temperature of hot stamping forming was determined to be 875 °C. The recrystallization mechanism in hot stamping of Ti6Al4V alloys was proposed based on EBSD tests on different sections of a hot stamping formed box-shaped component. With increasing deformation, the effect of dynamic recrystallization (DRX) was enhanced. When the thinning rate reached 15%, DRX surpassed dynamic recovery (DRV) as the dominant softening mechanism. DRX grains at different thinning rates were formed through both discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX), with CDRX always being the dominant mechanism.Keywords
Funding Information
- National Natural Science Foundation of China (51101072, 20210201038GX, 20230508039RC)
- Technology Development Program of Jilin Province (51101072, 20210201038GX, 20230508039RC)
- Program for Jilin University Science and Technology Innovative Research Team (51101072, 20210201038GX, 20230508039RC)
This publication has 38 references indexed in Scilit:
- Relationship between hot workability and texture evolution in an Al–Zn–Mg–Cu alloy under hot compressive stress modeJournal of Materials Science, 2023
- Microstructural Evolution, Intermetallic Formation, and Mechanical Performance of Dissimilar Al6061–Ti6Al4V Static Shoulder Friction Stir WeldsAdvanced Engineering Materials, 2023
- Microstructure Evolution and Anisotropy Effect During Low Temperature Cross Rolling and Annealing of Ti6Al4VMetallurgical and Materials Transactions A, 2023
- Microstructural Heterogeneity and Anisotropy Control of Additive Manufactured Ti-6Al-4V Alloy for Aircraft ComponentsJOM, 2023
- Substructure evolution in two phases based constitutive model for hot deformation of TC18 in α + β phase regionChinese Journal of Aeronautics, 2023
- Additive manufacturing of titanium-based alloys- A review of methods, properties, challenges, and prospectsHeliyon, 2022
- Constitutive modeling of softening mechanism and damage for Ti–6Al–4V alloy and its application in hot tensile simulation processArchives of Civil and Mechanical Engineering, 2021
- Numerical and experimental study on formability of TC4 alloy in a novel multi-layer sheet hot stamping processThe International Journal of Advanced Manufacturing Technology, 2020
- Phase transformation and dynamic recrystallization behaviors in a Ti55511 titanium alloy during hot compressionJournal of Alloys and Compounds, 2019
- Correlation between Flow Behavior and Microstructure Evolution during α/β Deformation of TA19 Titanium AlloyAdvanced Engineering Materials, 2016