Through the study of the thermal rheological behavior of Ti6Al4V alloy at different temperatures (500 °C, 600 °C, 700 °C, and 800 °C) and different strain rates (0.1 s⁻¹, 0.05 s⁻¹, 0.01 s⁻¹, and 0.005 s⁻¹), a constitutive model was developed for Ti6Al4V alloy across a wide temperature range in the hot stamping process. The model’s correlation coefficient reached 0.9847, indicating its high predictive accuracy. Hot processing maps suitable for the hot stamping process of Ti6Al4V alloy were developed, demonstrating the significant impact of the strain rate on the hot formability of Ti6Al4V alloy. At higher strain rates (>0.05 s⁻¹), the hot processing of Ti6Al4V alloy is less prone to instability. Combining hot processing maps with hot stamping experiments, it was found that the forming quality and thickness uniformity of parts improved significantly with the increase in stamping speed. The phase composition and microstructures of the forming parts under different heating temperature conditions have been investigated using SEM, EBSD, XRD, and TEM, and the maximum heating temperature of hot stamping forming was determined to be 875 °C. The recrystallization mechanism in hot stamping of Ti6Al4V alloys was proposed based on EBSD tests on different sections of a hot stamping formed box-shaped component. With increasing deformation, the effect of dynamic recrystallization (DRX) was enhanced. When the thinning rate reached 15%, DRX surpassed dynamic recovery (DRV) as the dominant softening mechanism. DRX grains at different thinning rates were formed through both discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX), with CDRX always being the dominant mechanism.

Titanium alloy hot stamping technology has a wide range of application prospects in the field of titanium alloy part processing due to its high production efficiency and low manufacturing cost. However, the challenges of forming titanium alloy parts with large depths and deformations have restricted its development. In this study, the hot stamping process of a Ti6Al4V alloy box-shaped part was investigated using ABAQUS 2020 software. The thermodynamic properties of a Ti6Al4V alloy sheet were explored at different temperatures (400 °C, 500 °C, 600 °C, 700 °C, 800 °C) and different strain rates (0.1 s⁻¹, 0.05 s⁻¹, 0.01 s⁻¹). In addition, the influence law of hot stamping process parameters on the minimum thickness of the formed part was revealed through the analysis of response surface methodology (RSM), ultimately obtaining the optimal combination of process parameters for Ti6Al4V alloy hot stamping. The experimental results of the hot stamping process exhibited a favorable correlation with the simulated outcomes, confirming the accuracy of the numerical simulation. The study on the microstructure evolution of the formed parts showed that grain refinement strengthening occurred in the part with large deformation, and the formed box-shaped parts exhibited a uniform and fine microstructure overall, demonstrating high forming quality. The achievements of the work provide important guidance for the fabrication of titanium alloy parts with large depths and deformations used in heavy industrial production.