Hongtao Ma

The microstructure, mechanical response, and failure behavior of lead free solder joints in electronic assemblies are constantly evolving when exposed to isothermal aging and/or thermal cycling environments. In our prior work on aging effects (Ma, et al., ECTC 2006), we demonstrated that the observed material behavior variations of SAC405 and SAC305 lead free solders during room temperature aging (25 °C) were unexpectedly large and universally detrimental to reliability. Such effects for lead free solder materials are much more dramatic at the higher aging temperatures (e.g. 100–150 °C) typical of the harsh environments present in high performance computing and in automotive, aerospace, and defense applications. However, there has been little work in the literature, and the work that has been done has concentrated on the degradation of solder ball shear strength (e.g. Dage Shear Tester). Current finite element models for solder joint reliability during thermal cycling accelerated life testing are based on traditional solder constitutive and failure models that do not evolve with material aging. Thus, there will be significant errors in the calculations with the new lead free SAC alloys that illustrate dramatic aging phenomena. In the current work, we have explored the effects of elevated temperature isothermal aging on the mechanical behavior and reliability of lead free solders. The effects of aging on mechanical behavior have been examined by performing stress-strain and creep tests on SAC405 and SAC305 samples that were aged for various durations (0–6 months) at several elevated temperatures (80, 100, 125, and 150 °C). Analogous tests were performed with 63Sn-37Pb eutectic solder samples for comparison purposes. Variations of the temperature dependent mechanical properties (elastic modulus, yield stress, ultimate strength, creep compliance, etc.) were observed and modeled as a function of aging time and temperature. In this paper, we have concentrated our efforts on presenting the results for samples aged at 125 °C. In addition, the new elevated temperature aging data were correlated with our room temperature results from last year’s investigation. The results obtained in this work have demonstrated the significant effects of elevated temperature exposure on solder joints. As expected, the mechanical properties evolved at a higher rate and experienced larger changes during elevated temperature aging (compared to room temperature aging). After approximately 200 hours of aging, the lead free solder joint material properties were observed to degrade at a nearly constant rate. We have developed a mathematical model to predict the variation of the properties with aging time and aging temperature. Our data for the evolution of the creep response of solders with elevated temperature aging show that the creep behavior of lead free and tin-lead solders experience a “crossover point” where lead free solders begin to creep at higher rates than standard 63Sn-37Pb solder for the same stress level. Such an effect is not observed for solder joints aged at room temperature, where SAC alloys always creep at lower rates than Sn-Pb solder.

Solder materials demonstrate evolving micro structure and mechanical behavior that changes significantly with environmental exposures such as isothermal aging and thermal cycling. These aging effects are greatly exacerbated at higher temperatures typical of thermal cycling qualification tests for harsh environment electronic packaging. In the current study, mechanical measurements of thermal aging effects and material behavior evolution of lead free solders have been performed. Extreme care has been taken so that the fabricated solder uniaxial test specimens accurately reflect the solder materials present in actual lead free solder joints. A novel specimen preparation procedure has been developed where the solder uniaxial test specimens are formed in high precision rectangular cross-section glass tubes using a vacuum suction process. The tubes are then sent through a SMT reflow to re-melt the solder in the tubes and subject them to any desired temperature profile (i.e. same as actual solder joints). Using specimens fabricated with the developed procedure, isothermal aging effects and viscoplastic material behavior evolution have been characterized for 95.5Sn-4.0Ag-0.5Cu (SAC405) and 96.5Sn-3.0Ag-0.5Cu (SAC305) lead free solders which are commonly used as the solder ball alloy in lead free BGAs and other components. Analogous tests were performed with 63Sn-37Pb eutectic solder samples for comparison purposes. In our total experimental program, samples have been solidified with both reflowed and water quenching temperature profiles, and isothermal aging has been performed at room temperature (25 degC) and elevated temperatures (100 degC, 125 degC and 150 degC). In this paper, we have concentrated on reporting the results of the room temperature aging experiments. Variations of the temperature dependent mechanical properties (elastic modulus, yield stress, ultimate strength, creep compliance, etc.) were observed and modeled as a function of room temperature aging time. Micro structural changes during room temperature aging have also been recorded for the solder alloys and correlated with the observed mechanical behavior changes