Kanghyun Kim

In this study, a three-dimensional (3D) porous sponge capable of oil–water separation was fabricated using recycled expanded polystyrene (EPS) through 3D electrospinning, by adding phosphoric acid to the electrospinning solution. The fabrication process was a rapid and efficient single-step process to produce the 3D sponge. In addition, the additive’s concentration was also optimized for oil absorption. The fabricated EPS sponge was highly effective in oil–water separation due to its excellent hydrophobic and oleophilic properties. This demonstrates its potential as a sustainable and efficient absorbent to address ongoing oil pollution issues. Moreover, the performance of the recycled EPS sponge was found to be comparable to that of sponges made from virgin polystyrene, suggesting the feasibility of using recycled materials for the production of high-value products. This research presents an efficient method for fabricating 3D sponges from recycled materials, contributing to environmental protection and resource recycling.

Oblique submicron-scale structures are used in various aspects of research, such as the directional characteristics of dry adhesives and wettability. Although deposition, etching, and lithography techniques are applied to fabricate oblique submicron-scale structures, these approaches have the problem of the controllability or throughput of the structures. Here, we propose a simple X-ray-lithography method, which can control the oblique angle of submicron-scale structures with areas on the centimeter scale. An X-ray mask was fabricated by gold film deposition on slanted structures. Using this mask, oblique ZEP520A photoresist structures with slopes of 20° and 10° and widths of 510 nm and 345 nm were fabricated by oblique X-ray exposure, and the possibility of polydimethylsiloxane (PDMS) molding was also confirmed. In addition, through double exposure with submicron- and micron-scale X-ray masks, dotted-line patterns were produced as an example of multiscale patterning.

Brain‒machine interface (BMI) is a promising technology that looks set to contribute to the development of artificial limbs and new input devices by integrating various recent technological advances, including neural electrodes, wireless communication, signal analysis, and robot control. Neural electrodes are a key technological component of BMI, as they can record the rapid and numerous signals emitted by neurons. To receive stable, consistent, and accurate signals, electrodes are designed in accordance with various templates using diverse materials. With the development of microelectromechanical systems (MEMS) technology, electrodes have become more integrated, and their performance has gradually evolved through surface modification and advances in biotechnology. In this paper, we review the development of the extracellular/intracellular type of in vitro microelectrode array (MEA) to investigate neural interface technology and the penetrating/surface (non-penetrating) type of in vivo electrodes. We briefly examine the history and study the recently developed shapes and various uses of the electrode. Also, electrode materials and surface modification techniques are reviewed to measure high-quality neural signals that can be used in BMI.

In this paper, we developed a method of fabricating polymer microstructures at various angles on a single substrate via synchrotron X-ray lithography coupled with simple dimensional transformations. Earlier efforts to create various three-dimensional (3D) features on flat substrates focused on the exposure technology, material properties, and light sources. A few research groups have sought to create microstructures on curved substrates. We created tilted microstructures of various angles by simply deforming the substrate from 3D to two-dimensional (2D). The microstructural inclination angles changed depending on the angles of the support at particular positions. We used convex, concave, and S-shaped supports to fabricate microstructures with high aspect ratios (1:11) and high inclination angles (to 79°). The method is simple and can be extended to various 3D microstructural applications; for example, the fabrication of microarrays for optical components, and tilted micro/nanochannels for biological applications.

Carbon nanotube (CNT) nanobundles are widely used in nanoscale imaging, fabrication, and electrochemical and biological sensing. The diameter of CNT nanobundles should be controlled precisely, because it is an important factor in determining electrode performance. Here, we fabricated CNT nanobundles on tungsten tips using dielectrophoresis (DEP) force and controlled their diameters by varying the withdrawal velocity of the tungsten tips. Withdrawal velocity pulling away from the liquid–air interface could be an important, reliable parameter to control the diameter of CNT nanobundles. The withdrawal velocity was controlled automatically and precisely with a one-dimensional motorized stage. The effect of the withdrawal velocity on the diameter of CNT nanobundles was analyzed theoretically and compared with the experimental results. Based on the attachment efficiency, the withdrawal velocity is inversely proportional to the diameter of the CNT nanobundles; this has been demonstrated experimentally. Control of the withdrawal velocity will play an important role in fabricating CNT nanobundles using DEP phenomena.