Diego Berti Salvaro

The dispersion stability of carbon-based solid lubricants/lubricating oils remains a challenge to overcome. Recently, novel processing routes were developed to obtain 2D turbostratic graphite particles via solid-state reactions between B₄C and Cr₃C₂ (GBC) and between SiC and Fe (GSF) that present outstanding tribological properties in a dry scenario, as well as functionalized graphene (GNH). This work investigated the suspension stability of GBC and GSF particles (0.05 wt.%) dispersed in a low-viscosity polyol ester lubricating oil and their tribological performance. Ammonia-functionalized graphene (GNH) particles were also used as a reference. In order to evaluate the dispersion stability, in addition to the classical digital image technique, a much more assertive, reliable, quantitative and rarely reported in the literature technique was used, i.e., the STEP^TM (Space and Time-resolved Extinction Profiles) technology. Reciprocating sphere-on-flat tribological tests were carried out, in which before contact, 0.2 μL of pure oil and suspension (POE + 0.05 wt.% of solid lubricant) was applied on a flat surface. The results showed that the GBC particles remained remarkably stable and reduced the sphere wear rate by 61.8%. From the tribosystem point of view, the presence of GBC and GSF reduced the wear rate by 18.4% and 2.2%, respectively, with respect to the pure oil, while the GNH particles increased the wear rate by 4.2%. Furthermore, the wear rate was improved due to the highly disordered carbon tribolayer formation identified on both surfaces.

Sintered iron-based self-lubricant composites in which graphite reservoirs are generated by the dissociation of silicon carbide (SiC) particles feature low friction coefficients and scuffing resistance combined with high mechanical stress. This work evaluated the influence of the sintering temperature and the SiC polytype on the graphite reservoirs morphology, structure, and friction behaviour. The reservoirs were studied by field emission gun-scanning electron microscopy (FEG-SEM), micro-Raman spectroscopy, and transmission electron microscopy (TEM). The friction behaviour was evaluated by cylinder on plane tests (friction coefficient and scuffing resistance). The results showed that the SiC polytype and the sintering temperature modified the graphite structures. The SiC dissociation promoted the formation of different nano graphites, presenting different turbostratic 2D and 3D arrays. The results showed that the presence of the turbostratic graphite was beneficial to the friction behaviour of these composites, which offered better tribological performance than the composite with 3D graphite.