In this paper, classical molecular dynamics simulations were used to explore the impact of deposition temperature and bias voltage on the growth of Al2O3 thin films through magnetron sputtering. Ion energy distributions were derived from plasma mass spectrometer measurements. The fluxes of deposited particles (Ar+, Al+, and O−) were categorized into low, medium, and high energies, and the results show that the films are dominated by amorphous Al2O3 at low incident energies without applying bias. As the deposition temperature increased, the crystallinity of the films also increased, with the crystals predominantly consisting of γ-Al2O3. The crystal content of the deposited films increased when biased with −20 V compared to when no bias was applied. Crystalline films were successfully obtained at a deposition temperature of 773 K with a −20 V bias. When biased with −40 V, crystals could be obtained at a lower deposition temperature of 573 K. Increasing the bias enables the particles to have higher energy to overcome the nucleation barrier of the crystallization process, leading to a greater degree of film crystallization. At this stage, the average bond length between Al-O is measured to be approximately 1.89 Å to 1.91 Å, closely resembling that of the crystal.

To fabricate high-quality polycrystalline VO₂ thin film with a metal–insulator transition (MIT) temperature less than 50 °C, high-power impulse magnetron sputtering with different discharge currents was employed in this study. The as-deposited VO₂ films were characterized by a four-point probe resistivity measurement system, visible-near infrared (IR) transmittance spectra, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy. The resistivity results revealed that all the as-deposited films had a high resistance change in the phase transition process, and the MIT temperature decreased with the increased discharge current, where little deterioration in the phase transition properties, such as the resistance and transmittance changes, could be found. Additionally, XRD patterns at various temperatures exhibited that some reverse deformations that existed in the MIT process of the VO₂ film, with a large amount of preferred crystalline orientations. The decrease of the MIT temperature with little deterioration on phase transition properties could be attributed to the reduction of the preferred grain orientations.