Chenxi Ji
Current Organizations / Institutes
The organizations/institutes from the scholar's latest article
Chenxi Ji has a total of 9 co-authors. Here are the top co-authors by number of shared publications:
- Guoliang Liu
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China
2 shared publications - Qing Liu
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing, P.R. China
2 shared publications - Bin Chen
Shougang Group Co., Ltd. Research Institute of Technology, Beijing 100043, China
1 shared publication - Bin Li
State Key Laboratory of Advanced Special Steel & Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200444, China
1 shared publication - Hai-Bo Li
Shougang Group Co., Ltd. Research Institute of Technology, Beijing 100043, China
1 shared publication - Haibiao Lu
School of Materials Science and Engineering, State Key Laboratory of Materials for Advanced Nuclear Energy, Shanghai University, Shanghai, P.R. China
1 shared publication
Latest Publications
- Open Access
Influence of M-EMS on Fluid Flow and Initial Solidification in Slab Continuous Casting
A mathematical model coupled with electromagnetic field has been developed to simulate the transient turbulence flow and initial solidification in a slab continuous casting mold under different electromagnetic stirring (EMS) currents and casting speeds. Through comparing the magnetic flux density, flow field with measured results, the reliability of the mathematical model is proved. The uniform index of solidified shell thickness has been introduced to judge the uniformity of the solidified shell. The results show that a horizonal recirculation flow has been generated when EMS is applied, and either accelerated or decelerated regions of flow field are formed in the liquid pool. Large EMS current and low casting speed may cause the plug flow near the mold narrow face and a suitable EMS current can benefit to the uniform growth of solidified shell. Meanwhile, an industrial test exhibits that EMS can weaken the level fluctuation and number density of inclusion. Overall, a rational EMS current range is gained, when the casting speed is 1.2 m/min, the rational EMS current is 500–600 A.
Open AccessInfluence of M-EMS on Fluid Flow and Initial Solidification in Slab Continuous Casting
A mathematical model coupled with electromagnetic field has been developed to simulate the transient turbulence flow and initial solidification in a slab continuous casting mold under different electromagnetic stirring (EMS) currents and casting speeds. Through comparing the magnetic flux density, flow field with measured results, the reliability of the mathematical model is proved. The uniform index of solidified shell thickness has been introduced to judge the uniformity of the solidified shell. The results show that a horizonal recirculation flow has been generated when EMS is applied, and either accelerated or decelerated regions of flow field are formed in the liquid pool. Large EMS current and low casting speed may cause the plug flow near the mold narrow face and a suitable EMS current can benefit to the uniform growth of solidified shell. Meanwhile, an industrial test exhibits that EMS can weaken the level fluctuation and number density of inclusion. Overall, a rational EMS current range is gained, when the casting speed is 1.2 m/min, the rational EMS current is 500–600 A.
- Open Access
Application of a Novel Chamfered Mold to Suppress Corner Transverse Cracking of Micro-Alloyed Steel Slabs
A novel chamfered mold is developed to solve the problem of corner transverse cracking in micro-alloyed steel slabs. The shape of the slab was changed from four corners and sides to eight corners and sides due to the use of a chamfered mold. Based on numerical simulation, the solidification and heat transfer of different steel grades in the mold are studied. The results reveal rapid solidification shrinkage of molten steel in the upper area of the mold and slow solidification shrinkage in the lower area; thus, a double-taper mold is designed according to these results. The first area of the variable taper falls in the range of 250–400 mm from the top of the mold, and the design method of double inclined water channels in the chamfered face is found to be the most helpful for the formation of a uniform initial shell and reducing hotspots of the mold. Actual production results show that the quality of the slab is better when the heat flux of the narrow face is larger than that of the broad face. Corner transverse cracking in micro-alloyed steels is greatly reduced from an incidence of 4.2% to less than 0.3%. In addition, the chamfered mold is applied in IF (interstitial free) steel production, and the edge quality of hot rolled sheets is found to also be dramatically improved.
Open AccessApplication of a Novel Chamfered Mold to Suppress Corner Transverse Cracking of Micro-Alloyed Steel Slabs
A novel chamfered mold is developed to solve the problem of corner transverse cracking in micro-alloyed steel slabs. The shape of the slab was changed from four corners and sides to eight corners and sides due to the use of a chamfered mold. Based on numerical simulation, the solidification and heat transfer of different steel grades in the mold are studied. The results reveal rapid solidification shrinkage of molten steel in the upper area of the mold and slow solidification shrinkage in the lower area; thus, a double-taper mold is designed according to these results. The first area of the variable taper falls in the range of 250–400 mm from the top of the mold, and the design method of double inclined water channels in the chamfered face is found to be the most helpful for the formation of a uniform initial shell and reducing hotspots of the mold. Actual production results show that the quality of the slab is better when the heat flux of the narrow face is larger than that of the broad face. Corner transverse cracking in micro-alloyed steels is greatly reduced from an incidence of 4.2% to less than 0.3%. In addition, the chamfered mold is applied in IF (interstitial free) steel production, and the edge quality of hot rolled sheets is found to also be dramatically improved.