Linchun Gao

The exposure of spaceborne devices to high-energy charged particles in space results in the occurrence of both a total ionizing dose (TID) and the single-event effect (SEE). These phenomena present significant challenges for the reliable operation of spacecraft and satellites. The rapid advancement of semiconductor fabrication processes and the continuous reduction in device feature size have led to an increase in the significance of the synergistic effects of TID and SEE in static random access memory (SRAM). In order to elucidate the involved physical mechanisms, the synergistic effects of TID and single-event upset (SEU) in a new kind of 130 nm 7T silicon-on-insulator (SOI) SRAM were investigated by means of cobalt-60 gamma-ray and heavy ion irradiation experiments. The findings demonstrate that 7T SOI SRAM is capable of maintaining normal reading and writing functionality when subjected to TID irradiation at a total dose of up to 750 krad(Si). In general, the TID was observed to reduce the SEU cross-section of the 7T SOI SRAM. However, the extent of this reduction was influenced by the heavy ion LET value and the specific writing data pattern employed. Based on the available evidence, it can be proposed that TID preirradiation represents a promising avenue for enhancing the resilience of 7T SOI SRAMs to SEU.

The ongoing trend towards miniaturization and increased packaging density has exacerbated the reliability problem of Au-Al heterogeneous metal bonding structures in high-temperature environments, where extreme temperatures and high current pose a serious challenge. In order to address this issue, the present study aims to investigate the electromigration reliability of Au-Al bonding by comparing the conventional heterogeneous contacts with OPM structures, which are homogeneous contacts. A novel bonding layout was developed to precisely detect the resistance and obtain stage changes in electromigration. The experimental results demonstrated that the relative resistance shift of Au-Al bonding at 250 °C was 98.7%, while CrAu and NiPdAu OPM structures exhibited only 46.1% and 2.93% shifts, which suggests that the reliability of OPM structures was improved by a factor of 2.14 and 33.6, respectively. The degradation of Au-Al bonding was attributed to the large cracks observed at the bonding interface and lateral consumption of Al elements. In contrast, OPM structures only exhibited tiny voids and maintained a better bonding state overall, indicating that homogeneous metal contacts have better immunity to electromigration. Furthermore, this study also observed the polarity effect of electromigration and analyzed the impact of NiPdAu thickness on reliability. Overall, this research provides a novel approach and an insightful theoretical reference for addressing the bottleneck of high-temperature electromigration reliability in high-temperature sensor packaging.

In this work, we present new evidence of the physical mechanism behind the generation of low-frequency noise with high interface-trap density by measuring the low-frequency noise magnitudes of partially depleted (PD) silicon-on-insulator (SOI) NMOSFETs as a function of irradiation dose. We measure the DC electrical characteristics of the devices at different irradiation doses and separate the threshold-voltage shifts caused by the oxide-trap charge and interface-trap charge. Moreover, the increased densities of the oxide-trap charge projected to the Si/SiO₂ interface and interface-trap charge are calculated. The results of our experiment suggest that the magnitudes of low-frequency noise do not necessarily increase with the increase in border-trap density. A novel physical explanation for the low-frequency noise in SOI-NMOSFETs with high interface-trap density is proposed. We reveal that the presence of high-density interface traps after irradiation has a repressing effect on the generation of low-frequency noise. Furthermore, the exchange of some carriers between border traps and interface traps can cause a decrease in the magnitude of low-frequency noise when the interface-trap density is high.

As a promising candidate in space radiation hardened applications, silicon-on-insulator (SOI) devices face the severe problem of total ionizing dose (TID) radiation because of the thick buried oxide (BOX) layer. The direct-current current–voltage (DCIV) method was applied for studying TID radiation of SOI metal–oxide–semiconductor field–effect transistors (MOSFETs) with different manufacture processes. It is found that the peak of high-voltage well (PX) devices shows a larger left-shift and a slower multitude increase along with radiation dose, compared with that of low-voltage well (PV) devices. It is illustrated that the high P-type impurity concentration near back interface makes it more difficult to break up silicon hydrogen bonds, which gives the PX devices superiority in resisting the build-up of interface traps. The study results indicate that increasing doping concentration of the body region near the back-gate interface might be an alternative radiation hardening technique of SOI MOSFET devices to avoid the parasitic back transistors’ leakage.