Enas Moustafa

Organic photovoltaic (OPV) cells have experienced significant development in the last decades after the introduction of nonfullerene acceptor molecules with top power conversion efficiencies reported over 19% and considerable versatility, for example, with application in transparent/semitransparent and flexible photovoltaics. Yet, the optimization of the operational stability continues to be a challenge. This study presents a comprehensive investigation of the use of a conjugated polyelectrolyte polymer (CPE-Na) as a hole layer (HTL) to improve the performance and longevity of OPV cells. Two different fabrication approaches were adopted: integrating CPE-Na with PEDOT:PSS to create a composite HTL and using CPE-Na as a stand-alone bilayer deposited beneath PEDOT:PSS on the ITO substrate. These configurations were compared against a reference device employing PEDOT:PSS alone, as the HTL increased efficiency and fill factor. The instruments with CPE-Na also demonstrated increased stability in the dark and under simulated operational conditions. Device-based PEDOT:PSS as an HTL reached T80 after 2500 h while involving CPE-Na in the device kept at T90 in the same period, evidenced by a reduced degradation rate. Furthermore, the impedance spectroscopy and photoinduced transient methods suggest optimized charge transfer and reduced charge carrier recombination. These findings collectively highlight the potential of CPE-Na as a HTL optimizer material for nonfluorine OPV cells.

Recently, there has been significant improvement in the power conversion efficiency of non-fullerene organic solar cells, exceeding 19%. In this article, we have fabricated conventional sandwich structure of ITO/PEDOT:PSS/PM6:Y7/PDINO/Ag reaching efficiency up to 17.3% along with high generated current density of 30.60 mA/cm2 for the optimized devices. The thickness of PM6:Y7 layer has been varied to investigate the impact on the overall device behavior. The obtained results showed that the PCE has been enhanced by 15% upon reducing its thickness from 150 nm to 100 nm. Accordingly, current-voltage measurements and impedance spectroscopy analysis through capacitance-voltage, Mott-Schottky analysis and capacitance frequency under different illumination intensities were conducted to evaluate the behaviour of the charge recombination due to thickness variation of the PM6:Y7 photoactive layer.

At present, low long-term stability is the main limitation for organic solar cells. The origin of the degradation of high-efficiency non-fullerene solar cells by impedance spectroscopy and its degradation mechanisms has been investigated.

Finding an effective approach to suppress trap formation is a potential route for enhancing the performance of nonfullerene organic photovoltaic (NF‐OPVs) devices. Here, an extraordinary short‐circuit current density (J_SC) value of 32.65 mA cm^‐2 is achieved, higher than the state‐of‐the art NF‐OPVs reported, reaching a high power conversion efficiency (PCE) of 17.92%. This remarkable enhancement is exhibited through the fine‐tuning of PEDOT:PSS/PM6:Y7 films and interface morphologies via applying the prethermal treatment approach (Pre‐TT) to the devices, which exhibit J_SC and PCE enhancement of 21% and 8%, respectively, compared to the pristine devices. Accordingly, the dependence of the J_SC upon the Pre‐TT approach through a range of morphological, optical, electrical, and advanced transient measurements is investigated. The Pre‐TT‐based films are found to possess optimal smooth blend morphology with better dispersity owing to reduced domain size. Moreover, the measurements show that the optimized treated devices present higher exciton dissociation probabilities and generation rate of the free charge carriers, showing an ideal balanced electron/hole mobility that reveals the J_SC and PCE enhancement. Hence, Pre‐TT approach provides a facile passivation strategy that reduces the trap state density of the blend film, improves interface charge transfer, allows balanced electron/hole mobility, and thus promotes device performance.

Morphological control of the layers within the bulk heterojunction organic photovoltaics (BHJ-OPVs) is a key feature that governs their performance. In the present work, we demonstrate that zinc oxide─ZnO─interlayers sprayed via the intermittent spray pyrolysis technique, employing a low-concentration precursor solution, can yield inverted BHJ-OPVs as efficient as the standard reported ones using the conventional laboratory-scale spin-coating technique. However, we record a pioneer stability behavior of the fabricated inverted fullerene organic photovoltaics (iF-OPVs) with various sprayed ZnO conditions. Thus, after optimizing the sprayed ZnO interfacial layer morphology for the inverted PTB7-Th:PC₇₀BM devices, by carefully inspecting the interdependence between the sprayed ZnO thin film morphology and the figures of merit of the optimized iF-OPVs, we conducted a distinct analysis on the optical and electronic properties of the fresh and degraded devices using external quantum efficiency measurements and impedance spectroscopy. Hence, we showed that the most proper ZnO microstructural morphology was obtained by spraying 25 running cycles (25R). Remarkably, we observed that 25R-ZnO-based iF-OPV devices showed a stunning stability behavior and maintained 85% of their initial power conversion efficiency even after 16.7 months without encapsulation in a dry nitrogen glovebox, demonstrating an excellent shelf stability. Accordingly, this approach might facilitate the scalability of inverted OPVs for industrial production visibility.