José Angel Hernández-Jiménez

In this work, a photo-polymerization route was used to obtain potassium acrylate-co-acrylamide hydrogels with enhanced mechanical properties, well-defined microstructures in the dry state, and unique meso- and macrostructures in the hydrated state. The properties of the hydrogels depended on the concentration of the crosslinking agent. Mechanical properties, swelling capacity, and morphology were analyzed, showing a well-defined transition at a critical concentration of the crosslinker. In terms of morphology, shape-evolving surface patterns appeared at different scales during swelling. These surface structures had a noticeable influence on the mechanical properties. Hydrogels with structures exhibited better mechanical properties compared to unstructured hydrogels. The critical crosslinking concentration reported in this work (using glycerol diacrylate) is a reference point for the future preparation of multistructured acrylic hydrogel with enhanced properties.

Compared to other fibrous materials, plant fibers can act as a reinforcement in plastics due to their relatively high strength and rigidity, low cost, low density, biodegradability, and renewability. In this context, this study examines the effect of the particle size and content of white oak wood flour (Quercus laeta Liemb), obtained from its branches, on the properties of commercial polypropylene. In Mexico, wood from the branches of Quercus laeta Liemb is barely utilized despite its abundance and viability. The main objective of this study is to demonstrate that this waste material can be exploited to prepare useful materials, in this case composites with competitive properties. Tensile and flexural tests, as well as impact strength and melt flow index were evaluated. In addition, density and water absorption capacity were also tested. Results showed that the water absorption increased with the incorporation of wood particles. Mechanical properties were strongly influenced by particle content. A reduction in elongation and strength was observed, while Young’s modulus and flexural modulus increased with the incorporation of wood particles. Impact strength increased with particle size and particle content.