Igor V. Suminov

One of the limitations of additive manufacturing technology is the high surface roughness of finished products caused by the layered structure of the deposition and the effect of adhesion of unfused powder particles. This worsens the fatigue characteristics, wear resistance, and functional properties of the parts, which are especially important for critical applications in medicine, aviation, and mechanical engineering. The paper presents the results of a study on the possibility of using plasma electrolytic polishing for post-processing of products made of additively manufactured Ti6Al4V alloy to form a homogeneous surface with reduced roughness. The morphology, roughness, and tribotechnical characteristics of the surface after processing in a fluoride electrolyte were studied with varying voltage and polishing time. A 90% reduction in surface roughness is achieved by polishing at 300 V for 20 min. The results of tribological tests revealed that after the polishing of the oxidative wear mechanism is maintained, the temperature in the tribological contact zone decreases, and the load-bearing capacity of the surface increases (the Kragelsky–Kombalov criterion decreases). The greatest decrease in the friction coefficient by 2.1 times was observed with minimal surface roughness, when the largest average radius of rounding of the microprotrusions of the friction track microtopology is formed with a low value of the Kragelsky–Kombalov criterion.

Nitriding is one of the technologies used to improve the performance properties of tool steels. In addition to traditional gas nitriding, technologies aimed at increasing the productivity and/or efficiency of processing have found application in industry. This paper presents the results of using vacuum and plasma electrolytic nitriding to improve the wear resistance of M2 high-speed steel, as well as prospects for further development of these technologies. XRD and SEM methods were used to study the structural and phase changes in the surface layers, showing the formation of layers of connections hardened to 1200–1300 HV. Tribological tests were carried out under dry friction conditions according to the shaft-shoe scheme with varying sliding speed. The mechanism of contact interaction during the friction of nitrided steel was established. It is shown that plastic deformations are the prevailing type of deformation. The mechanism of destruction of the surface layer is fatigue wear during dry friction without lubrication. This provides an increase in wear resistance by 6–29 times.

The positive effect of plasma electrolytic treatment on CrWMn tool steel to increase the wear resistance of its surface is shown. The effect of plasma electrolytic nitriding and subsequent polishing on the structure, phase and elemental composition, microhardness of the surface layer, and surface morphology is established. Steel nitriding leads to the formation of a modified surface layer including Fe_2–3N iron nitride and nitrogen martensite, below which hardening martensite is formed, reaching a microhardness value of 1200 HV. Subsequent polishing leads to a decrease in surface roughness by 42–68%. Tribological tests were carried out according to the shaft-bushing scheme. A decrease in the friction coefficient and weight wear of up to 2.6 and 30.1 times, respectively, is shown. The formed structure of the surface layer compensates for the effect of the counter body and determines the destruction of friction bonds by plastic displacement. The wear mechanism has been established and is defined as fatigue wear under dry friction and plastic contact.

The paper examines the possibility of increasing the wear and corrosion resistance of a CP-Ti surface by duplex plasma electrolytic treatment (borocarburizing and polishing). The structure and composition of diffusion layers, their microhardness, surface morphology and roughness, wear resistance during dry friction and corrosion resistance in Ringer’s solution were studied. The formation of a surface-hardened layer up to 200 μm thick with a microhardness of up to 950 HV, including carbides and a solid solution of boron and carbon, is shown. Subsequent polishing makes it possible to reduce surface roughness and remove weak areas of the porous oxide layer, which are formed during high-temperature oxidation in aqueous electrolyte vapor during borocarburizing. Changing the morphology and structural-phase composition of the CP-Ti surface helps reduce weight wear by a factor of three (the mode of frictional interaction changes from microcutting to oxidative wear) and corrosion current density by a factor of four after borocarburizing in a solution of boric acid, glycerin and ammonium chloride at 950 °C for 5 min and subsequent polishing in an ammonium fluoride solution at a voltage of 250 V for 3 min.

The paper investigates the feasibility of plasma electrolytic treatment (PET) of 90CrSi tool steel to enhance hardness and wear resistance. The influence of electrophysical parameters of PET (polarity of the active electrode, chemical-thermal treatment, and polishing modes) on the composition, structure, morphology, and tribological properties of the surface was studied. Tribological tests were carried out under dry friction conditions according to the shaft-bushing scheme with fixation of the friction coefficient and temperature in the friction contact zone, measurements of surface microgeometry parameters, morphological analysis of friction tracks, and weight wear. The formation of a surface hardened to 1110–1120 HV due to the formation of quenched martensite is shown. Features of nitrogen diffusion during anodic PET and cathodic PET were revealed, and diffusion coefficients were calculated. The wear resistance of the surface of 90CrSi steel increased by 5–9 times after anodic PET followed by polishing, by 16 times after cathodic PET, and up to 32 times after subsequent polishing. It is shown that in all cases, the violation of frictional bonds occurs through the plastic displacement of the material, and the wear mechanism is fatigue wear during dry friction and plastic contact.

The paper examines the possibility of increasing the wear and corrosion resistance of a CP-Ti surface by duplex plasma electrolytic treatment (borocarburizing and polishing). The structure and composition of diffusion layers, their microhardness, surface morphology and roughness, wear resistance during dry friction and corrosion resistance in Ringer's solution were studied. The formation of a surface hardened layer up to 200 m thick with a microhardness of up to 950 HV, including carbides and a solid solution of boron and carbon, is shown. Subsequent polishing makes it possible to reduce surface roughness and remove weak areas of the porous oxide layer, which is formed during high-temperature oxidation in aqueous electrolyte vapor during borocarburizing. Changing the morphology and structural-phase composition of the CP-Ti surface helps reduce weight wear by 3 times (the mode of frictional interaction changes from microcutting to oxidative wear) and corrosion current density by 4 times after borocarburizing in a solution of boric acid, glycerin and ammonium chloride at 950 °C for 5 minutes and subsequent polishing in an ammonium fluoride solution at a voltage of 250 V for 3 minutes.

The effect of plasma electrolytic nitrocarburizing on the wear resistance of carbon tool steel in friction couples with hardened steel and lead-tin bronze is considered in order to study the mechanism and type of wear, as well as the influence of structural and morphological characteristics of the surface on them. The microgeometry of friction tracks and its change with an increasing duration of friction tests are analyzed. The equilibrium roughness is determined, which is optimal for the friction couple and ensures minimal wear. The optimal values of the plasma electrolytic nitrocarburizing parameters, which provide the lowest values of the friction coefficient and wear rate, have been determined. The phase and elemental composition of the surface layer was studied using X-ray diffraction analysis and EDX analysis. The relationship of the microstructure of the nitrocarburized layer of tool steel with the friction coefficient and weight wear is established.

The effect of plasma electrolytic nitrocarburizing on the wear resistance of carbon tool steel in friction couples with hardened steel and lead-tin bronze is considered. The microgeometry of friction tracks and its change with increasing duration of friction tests are analyzed. The equilibrium roughness is determined, which is optimal for the friction couple and ensures minimal wear. The type and mechanism of wear of carbon tool steel after plasma electrolytic nitrocarburizing has been determined. The optimal values of the plasma electrolytic nitrocarburizing parameters, which provide the lowest values of the friction coefficient and weight wear, have been determined. The phase and elemental composition of the surface layer was studied using X-ray diffraction analysis and EDX analysis. The relationship of the microstructure of the nitrocarburized layer of tool steel with the friction coefficient and weight wear is established.