Malak Hamieh

In this study, chromium ferrite (FeCr; CrFe₂O₄) nanoparticles supported on activated carbon (AC), obtained from agricultural olive mill solid waste, were synthesized via a simple hydrothermal process. The structural, morphological, optical, and chemical properties of the FeCr/AC composite were characterized using XRD, SEM, EDX, DRS, BET, and FTIR techniques. The FeCr/AC composite was applied as a heterogeneous photo-Fenton catalyst for the degradation of methylene blue (MB) dye in an aqueous solution under 25 W visible-light LED irradiation. Critical operational factors, such as FeCr/AC dosage, pH, MB concentration, and H₂O₂ levels, were optimized. Under optimal conditions, 97.56% of MB was removed within 120 min of visible-light exposure, following pseudo-first-order kinetics. The composite also exhibited high efficiency in degrading methyl orange dye (95%) and tetracycline antibiotic (88%) within 180 min, with corresponding first-order rate constants of 0.0225 min⁻¹ and 0.0115 min⁻¹, respectively. This study highlights the potential of FeCr/AC for treating water contaminated with dyes and pharmaceuticals, in line with the Sustainable Development Goals (SDGs) for water purification.

In this study, chromium ferrite (FeCr; CrFe₂O₄) nanoparticles supported on activated carbon (AC), obtained from agricultural olive mill solid waste, were synthesized via a simple hydrothermal process. The structural, morphological, optical, and chemical properties of the FeCr/AC composite were characterized using XRD, SEM, EDX, DRS, BET, and FTIR techniques. The FeCr/AC composite was applied as a heterogeneous photo-Fenton catalyst for the degradation of methylene blue (MB) dye in aqueous solution under 25 W visible light LED irradiation. Critical operational factors such as FeCr/AC dosage, pH, MB concentration, and H₂O₂ levels were optimized. Under optimal conditions, 97.56% of MB was removed within 120 minutes of visible light exposure, following pseudo-first-order kinetics. The composite also exhibited high efficiency in degrading methyl orange dye (95%) and tetracycline antibiotic (88%) within 180 minutes, with corresponding first-order rate constants of 0.0225 min⁻¹ and 0.0115 min⁻¹, respectively. This study highlights the potential of FeCr/AC for treating water contaminated with dyes and pharmaceuticals, in line with the Sustainable Development Goals (SDGs) for water purification.

Ensuring effective water purification is essential for addressing freshwater scarcity and achieving the United Nations Sustainable Development Goals (SDGs). An efficient hybrid mixture, composed of FeCr quantum dots doped into mesoporous silica SBA-15 support and activated carbon (AC) derived from olive mill solid wastes, has been developed for treating high optical density polluted aqueous environments. This hybrid, denoted as FeCr-SBA-15/AC, was examined for its efficacy in the adsorption and photo-Fenton degradation of met orange dye (MO), a model high-optical-density pollutant, under visible light exposure. Characterization of the prepared samples was conducted using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), Brunauer–Emmett–Teller (BET) surface area analysis, diffuse reflectance spectroscopy (DRS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Key parameters investigated included catalyst dosage, dye concentration, solution pH, and H₂O₂ concentration. Remarkably, the FeCr-SBA-15/AC hybrid exhibited superior photocatalytic activity, achieving a degradation efficiency of 97% for MO under optimized conditions (catalyst dosage = 0.75 g L⁻¹, dye concentration = 20 mg L⁻¹, pH = 5.47, and 0.5 mL H₂O₂) after 180 min of irradiation with visible light. This performance surpassed that of FeCr-SBA-15 alone by 20%, due to the synergistic effects of adsorption and photo-Fenton. The adsorption of MO onto AC followed the Freundlich model equilibrium isotherm, while the experimental data for the hybrid mixture aligned well with the pseudo-first-order Langmuir–Hinshelwood kinetic model with a rate constant of 0.0173 min⁻¹. The leaching of Cr in the solution was very low—0.1 ppm—which is below the detection limit. These findings underscore the potential of the synthesized FeCr-SBA-15/AC hybrid as a cost-effective, environmentally friendly, and highly efficient photo-Fenton catalyst for treating wastewater contaminated by industrial effluents.

Industrial wastewater discharge, tainted with hazardous substances, including dyes like methylene blue (MB) from the textile sector, further emphasizes the need for water treatment to produce safe drinking water. This study explores the potential of olive mill solid waste, an abundant and cost-effective agricultural waste in Mediterranean regions, to yield high-quality activated carbon (AC) with zinc chloride activation for MB adsorption. The activation process, carried out at a modest temperature of 500 °C without the need for an inert atmosphere, resulted in AC with remarkable characteristics, boasting a substantial surface area of 1184 cm²·g⁻¹ and a total pore volume of 0.824 cm³·g⁻¹. Extensive characterization of the AC was carried out through a large range of surface techniques. The pH of the solution had minimal influence on MB adsorption, the maximum removal was 95%, which was under slightly acidic pH conditions (5.8), and the adsorbent dose was 0.4 g·L⁻¹ for a 50 mg·L⁻¹ MB concentration. Equilibrium data pertaining to MB adsorption were subjected to fitting with different models, namely Langmuir, Freundlich, and Temkin. Notably, the Langmuir model exhibited the best fit, revealing a maximum monolayer adsorption capacity of 500 mg·g⁻¹ at 25 °C, and the adsorption kinetics closely followed a pseudo-second-order model.

The SBA-15 loaded with methylene blue was successfully prepared by sample adsorption of methylene blue in SBA-15 and is characterized by an XRD, SEM, FTIR, and BET. The photocatalytic activity for methyl orange (MO) degradation was investigated under visible light irradiation under LEDs. Experimental results demonstrate that the SBA-15-MB exhibited higher photocatalytic activity than SBA-15 under visible light irradiation. The degradation efficiency of MO (50 ppm) by SBA-15-MB could reach 80% within 180 min under 25W LED visible light. The photocatalytic activity of SBA-15 could be attributed to the excitation of methylene blue by visible light, the transfer of electrons from methylene blue to SBA-15, and the production of radicals at the surface of SBA-15.

Ensuring access to affordable water treatment systems is paramount, given the dire situation where millions are deprived of clean drinking water. Industrial wastewater discharge, tainted with hazardous substances, including dyes like methylene blue (MB) from the textile sector, further emphasizes the need for water treatment to produce safe drinking water. This study explores the potential of Olive Mill Solid Waste (OMSW), an abundant and cost-effective agricultural waste in Mediterranean regions, to yield high-quality activated carbon (AC) with zinc chloride (ZnCl₂) activation for MB adsorption. The activation process, carried out at a modest temperature of 500°C without the need for an inert atmosphere, resulted in AC with remarkable characteristics, boasting a substantial surface area of 1,184 cm².g^− 1 and a total pore volume of 0.824 cm³.g^− 1. Extensive characterization of the AC was carried out through diverse techniques; Fourier Transform Infrared Spectroscopy (FT-IR), X-Ray Diffractometry (XRD), Brunauer, Emmett and Teller (BET) analysis, Zeta potential, Scanning Electron Microscopy (SEM), and Energy Dispersive X-ray (EDX) spectroscopy. The adsorption performance of the prepared AC was thoroughly evaluated through a comprehensive examination of various factors, including initial dye concentration, contact time, adsorbent dosage, and solution pH. The pH of the solution had minimal influence on MB adsorption, the maximum removal was 95% which was under slightly acidic pH conditions (5.8) and with an adsorbent dose of 0.4 g.L^− 1 for a 50 mg.L^− 1 MB concentration. Equilibrium data pertaining to MB adsorption were subjected to fitting with different models, namely Langmuir, Freundlich, and Temkin. Notably, the Langmuir model exhibited the best fit, revealing a maximum monolayer adsorption capacity of 500 mg.g^− 1 at 25°C, and the adsorption kinetics closely followed a pseudo-second order model. These experimental results underscore the promising potential of Olive Mill Solid Waste (OMSW) as an affordable adsorbent for MB, hinting at its applicability for a diverse array of pollutant removal scenarios.