Ziyang Zhou

La-doped ZnO nanoclusters confined within mesoporous SBA-15 were synthesized using an impregnation–calcination method and evaluated for their visible-light-driven photocatalytic degradation of Rhodamine B (RhB). Small-angle X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the preservation of the 2D hexagonal mesostructure of SBA-15 post-loading. In contrast, wide-angle XRD and Fourier-transform infrared spectroscopy (FT-IR) analyses revealed that the incorporated ZnO existed predominantly as highly dispersed amorphous or ultrafine clusters within the mesopores. N₂ adsorption–desorption measurements exhibited Type IV isotherms with H1 hysteresis loops. Compared to pristine SBA-15, the specific surface area and pore volume of the composites decreased from 729.35 m² g⁻¹ to 521.32 m² g⁻¹ and from 1.09 cm³ g⁻¹ to 0.85 cm³ g⁻¹, respectively, accompanied by an apparent increase in the average pore diameter from 5.99 nm to 6.55 nm, attributed to non-uniform pore occupation. Under visible-light irradiation, the photocatalytic performance was highly dependent on the La doping level. Notably, the 5% La-ZnO/SBA-15 sample exhibited superior activity, achieving over 99% RhB removal within 40 min and demonstrating the highest apparent rate constant (k = 0.1152 min⁻¹), surpassing both undoped ZnO/SBA-15 (k = 0.0467 min⁻¹) and other doping levels. Reusability tests over four consecutive cycles showed a consistent degradation efficiency exceeding 93%, with only a ~7 percentage-point decline, indicating excellent structural stability and recyclability. Radical scavenging experiments identified h⁺, ·OH, and ·O₂⁻ as the primary reactive species. Furthermore, photoluminescence (PL) quenching observed at the optimal 5% La doping level suggested suppressed radiative recombination and enhanced charge carrier separation. Collectively, these results underscore the synergistic effect of La doping and mesoporous confinement in achieving fast, efficient, and recyclable photocatalytic degradation of organic pollutants.

This study explores the fabrication of ZnO-SiO₂ composite films on silicon substrates via a sol–gel method combined with spin-coating, followed by annealing at various temperatures. The research aims to enhance the UV emission and photoelectric properties of the films. XRD showed that the prepared ZnO sample has a hexagonal structure. SEM images revealed the formation of ZnO nanorods within a dense SiO₂ substrate, ranging from 10 μm to 30 μm in length. Photoluminescent analysis showed that the film exhibited strong UV emission centered at 360 nm. The response time measurements indicated that the optimal photoresponse time was approximately 2.9 s. These results suggest the potential of ZnO-SiO₂ films as efficient UV-emitting materials with high photoconductivity and a stably reproducible response under visible light, thereby laying the foundation for their application in advanced optoelectronic devices.