Enhancing the Solar-Blind UV Detection Performance of β-Ga2O3 Films Through Oxygen Plasma Treatment

Authors:
Open Access
Publisher website
Google Scholar
Abstract
This study systematically investigated the effects of oxygen plasma treatment on oxygen vacancy defects in sputtered β-gallium oxide (β-Ga2O3) films and their corresponding ultraviolet (UV) detection performance. The sputtered β-Ga2O3 film subjected to 1 min of oxygen plasma treatment exhibited optimal photodetection properties. Compared to the untreated sample, the dark current was reduced by approximately one order of magnitude to 0.378 pA at 10 V bias. It exhibited an 86% (from 2.92 s to 0.41 s) decrease in response time, a 41.6% increase in photocurrent, a very high photo-to-dark current ratio of 9.18 × 105, and a specific detectivity of 2.62 × 1010 cm·Hz1/2W−1 under 254 nm UV illumination intensity of 799 μW/cm2 at 10 V bias. Notably, appropriate oxygen plasma treatment minimizes electron capture, enhances the separation and collection of photogenerated carriers, and suppresses the persistent photoconductivity (PPC) effect, thus ultimately shortening the response time. Oxygen plasma processing thus provides an effective approach to fabricating high-performance β-Ga2O3 solar-blind photodetectors (SBPDs).
Funding Information
  • National Natural Science Foundation of China (62173128, 62303166)
  • Natural Science Foundation of Henan Province (252300421296)
  • Key Project of Scientific and Technology Research of Henan Province (252102210201)
  • Henan Province Office of Education (25A510013, 24B510007)
  • Henan Polytechnic University (J2025-6)

This publication has 38 references indexed in Scilit: