Wet high-energy milling and uniaxial pressing are used to fabricate CaO-stabilized tetragonal zirconia polycrystalline ceramic (Ca-TZP) with decent mechanical characteristics, i.e., a hardness of 11.5 GPa, Young’s modulus of 230 GPa, and fracture toughness of 13 MPa·m0.5. The effect of CaO concentration and the sintering temperature on phase composition and mechanical characteristics of CaO-stabilized zirconia ceramic made of baddeleyite is investigated.Keywords
Funding Information
- Russian Foundation for Basic Research (18-29-17047)
This publication has 12 references indexed in Scilit:
- Zirconia based ceramics, some clinical and biological aspects: ReviewFuture Dental Journal, 2016
- Zirconia based dental ceramics: structure, mechanical properties, biocompatibility and applicationsDalton Transactions, 2016
- Characteristics and performance of CaO-based high temperature CO2 sorbents derived from a sol–gel process with different supportsRSC Advances, 2016
- Preparation of Nanocrystalline Calcia‐Stabilized Tetragonal Zirconia by High‐Energy Milling of BaddeleyiteInternational Journal of Applied Ceramic Technology, 2015
- The Tetragonal‐Monoclinic Transformation in Zirconia: Lessons Learned and Future TrendsJournal of the American Ceramic Society, 2009
- Stabilized zirconia as a structural ceramic: An overviewDental Materials, 2008
- Zirconium-Containing Materials for Ceramics and Refractories Manufactured from Baddeleyite-Containing Products of the Kovdorskii Mining-and-Dressing Works Joint-Stock Co.Refractories and Industrial Ceramics, 2002
- Effect of Agglomeration on Mechanical Properties of Porous Zirconia Fabricated by Partial SinteringJournal of the American Ceramic Society, 2002
- CaO-containing tetragonal ZrO2 polycrystals (Ca-TZP)Ceramics International, 1987
- A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack MeasurementsJournal of the American Ceramic Society, 1981