Svetlana S. Razlivalova

This study investigated the concentration-dependent effects of zinc oxide nanoparticles (ZnO NPs, 30–70 nm) on the freshwater microalga Lobosphaera sp. under different salinity conditions (0–4 g L⁻¹ NaCl). ZnO NPs demonstrated dual effects: low concentration (0.75 mg L⁻¹) enhanced growth and alleviated salt stress, while higher concentrations (7.5–75 mg L⁻¹) caused significant growth inhibition (up to 52%) and induced oxidative stress. Salinity did not significantly affect NPs aggregation patterns, and neither salinity nor aggregation degree influenced toxicity outcomes. NPs concentration plays a dominant role of toxicological effects. Dose-dependent increases in catalase activity and ROS-positive cells confirmed NPs-induced oxidative stress. Crucially, zinc bioaccumulation correlated with NPs concentration but dissociated from dissolved Zn²⁺ release, demonstrating particle-driven toxicity. Our findings challenge the ion-release paradigm and highlight the potential of low-dose ZnO nanoparticles as effective stress-protectors in algal biotechnology, offering new strategies for enhancing microalgal resilience under environmental stress.

Copper (II) oxide nanoparticles (CuO NPs) attract much attention as a promising antimicrobial agent. We studied the antibacterial properties of three types of CuO NPs against Escherichia coli bacteria: flake-shaped particles with a diameter of 50–200 nm and a thickness of 10–20 nm (CuO-CD synthesized by chemical deposition), spherical particles with a size of 20–90 nm (CuO-EE obtained by electrical explosion), and rod-shaped particles with a length of 100–200 nm and a diameter of 30 × 70 nm (CuO-CS commercial sample). We tested how the shape, size, and concentration of the NPs, and composition of the dispersion medium affected the properties of the CuO NPs. We prepared dispersions based on distilled water, a 0.9% NaCl solution, and the LB broth by Lennox and used Triton X-100 and sodium dodecyl sulfate (SDS) as stabilizers. The concentration of NPs was 1–100 mg L⁻¹. We showed that the dispersion medium composition and stabilizer type had the greatest influence on the antibacterial effects of CuO NPs. We observed the maximum antibacterial effect for all CuO NP types dispersed in water without a stabilizer, as well as in LB broth with the SDS stabilizer. The maximum inhibition of culture growth was observed under the influence of CuO-EE (by 30%) and in the LB broth with the SDS stabilizer (by 1.3–1.8 times depending on the type of particles). In the saline solution, the antibacterial effects were minimal; in some cases, the CuO NPs even promoted bacterial culture growth. SDS increased the antibacterial effects of NPs in broth and saline but decreased them in water. Finally, among the particle types, CuO-CS turned out to be the most bactericidal, which is probably due to their rod-shaped morphology and small diameter. At the same time, the concentration and aggregation effects of CuO NPs in the colloidal systems we studied did not have a linear action on their antibacterial properties. These results can be used in the development of antibacterial coatings and preparations based on CuO NPs to achieve their maximum efficiency, taking into account the expected conditions of their use.

Extensive development of the Arctic, rich in various natural resources, requires a lot of cheap ecologically safe construction materials preferably using local renewable sources. Ice being easily available in regions with a cold climate meets all the above criteria but has low strength, high fragility and a tendency to creep. Known strengthening techniques using macroscopic and microfiber additives have many drawbacks. This paper describes a new approach to ice strengthening by adding organic or inorganic 50–100 nm nanoparticles (NPs) to the water to be frozen and presents experimental results and possible mechanisms analysis of polycrystalline ice strengthening using NPs. Cellulose and silica NPs have been tested as typical representatives of such additives. Both are hydrophilic, ecologically safe, widespread, cheap and can be produced from local renewable raw materials. It is shown that the addition of 0.01 to 5 wt.% of NPs results in a reduction of ice composite average grain size by a factor of 5.3 ± 0.7 and an increase of its compression strength by a factor of 2.5 ± 0.3. The highest sensitivity of ice strength to NPs concentration is between 0.1 and 1 wt.%. In this concentration range, the increase in strength is reversely proportional to the square root of the average grain size. Experimental data fit Griffith’s relation better than Hall–Petch, so ice strength is limited by cracks with the length proportional to average grain size.

A Zr-doped CaO sorbent for high-temperature CO₂ capture was fabricated using electrospinning. The nanofiber sorbent with an average filament diameter of about 160 nm is characterized by an initial CO₂ uptake capacity of 12.1 mmol/g, a specific surface area of 79 m²/g, an indentation Young’s modulus of 520 MPa, and a hardness of 1.6 MPa. After 50 carbonation/decarbonation cycles, the sorbent has a decent CO₂ uptake capacity of 9.7 mmol/g due to the uniform distribution of CaZrO₃ in the CaO nanofibers to prevent CaO grain growth caused by CaCO₃ sintering. It is revealed that the sorbent CO₂ uptake capacity decreases both with an increase in the decarbonation temperature and with an increase in the CO₂ concentration in the gas flow upon carbonation, where the sorbent CO₂ uptake capacity is more sensitive to the decarbonation temperature than to the CO₂ concentration in the gaseous stream during carbonation. It is assumed that the electrospun regenerable Zr-doped CaO sorbent is effective for removing CO₂ from flue gases.

Ice as a construction material has a number of advantages in Arctics. It is local renewable ecologically safe resource, and it does not require supplying from mainland. However, mechanical characteristics of natural ice is rather low. Potential of known techniques of ice strengthening employing reinforcement by microfibers or macroscopic components is limited. The paper describes strengthening of ice matrix using nanodisperce silica particles. Sixfold reduction of grain size induced by adding 10% wt of SiO2 nanoparticles results in 2.5 times increase in strength limit in uniaxial compression test and more than an order of magnitude increase in fracture energy.

The nanofibrous CaO sorbent for high-temperature CO₂ capture was fabricated by the calcination of electrospun composite filaments containing calcium acetylacetonate and polyacrylonitrile as a calcium-oxide precursor and a binder polymer, respectively. The calcination was carried out in air to prevent PAN carbonization and to obtain pure CaO nanofibers. The resulting mats of CaO nanofibers with the average diameter of 130 nm were characterized by a specific surface area of 31 m²/g, a CO₂-uptake capacity of 16.4 mmol/g at the carbonation temperature of 618 °C, a hardness of 1.87 MPa, and the indentation Young’s modulus of 786 MPa. The low decarbonation temperature makes the fabricated sorbent promising, for example, for the calcium-looping technology of CO₂ removal from the hot exhaust gases of fossil-fueled power plants.

Zirconia nanofiber mats containing filaments with the average diameter of less than 100 nm were fabricated. It is found that the hardness and Young’s modulus of the mats are sensitive to the microstructure, phase composition and average diameter of the zirconia nanofibers. The hardness and Young’s modulus of the prepared zirconia nanofiber mats vary from 0.86 to 1.67 MPa and from 133 to 362 MPa, respectively, wherein an increase in hardness is accompanied by the rise in Young’s modulus.

Wet high-energy milling and uniaxial pressing are used to fabricate CaO-stabilized tetragonal zirconia polycrystalline ceramic (Ca-TZP) with decent mechanical characteristics, i.e., a hardness of 11.5 GPa, Young’s modulus of 230 GPa, and fracture toughness of 13 MPa·m^0.5. The effect of CaO concentration and the sintering temperature on phase composition and mechanical characteristics of CaO-stabilized zirconia ceramic made of baddeleyite is investigated.

The effect of cyclic carbonation–decarbonation operating parameters on Zr-doped CaO sorbent CO₂ uptake capacity evolution is examined. It is revealed that the capacity steady state value increases with the decrease in the carbonation temperature, CO₂ concentration in the gas flow upon carbonation and with the increase in the heating rate from the carbonation to the decarbonation stages. The rise in decarbonation temperature leads to a dramatic decrease in the sorbent performance. It is found that if carbonation occurs at 630 °C in the gas flow containing 15 vol.% CO₂ and decarbonation is carried out at 742 °C, the sorbent shows the highest values of the initial and steady state CO₂ uptake capacity, namely, 10.7 mmol/g and 9.4 mmol/g, respectively.

The mats of yttria-stabilized tetragonal zirconia nanofibers were prepared using electrospinning. The effect of calcination temperature in the range of 600–1200 °C on their microstructure, phase composition and mechanical properties was investigated. Phase composition of the nanofibers did not change in all ranges of the calcination temperatures, while the average grain size increased from 8 to 39 nm. Nanoindentation testing of the mats showed a decrease in the hysteresis loop energy in samples with higher calcination temperature. Hardness and the elastic modulus measured with the indentation technique were the highest for the mats calcined at 900 °C.